公司信息及水印






牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种可着色的特种热塑性硫化弹性体(TPV)。 它专为与 PC、ABS、PC/ABS 和 PMMA 粘结而配制,适用于要求硬/软材料组合的应 用。这一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型或 挤出成型设备上加工。可在线回收利用。 A colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to PC, ABS, PC/ABS, ASA and PMMA for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
密度 Density |
1.06 | g/cm³ | ISO 1183 |
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
8.00 | MPa | ISO 37 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
注册或登录后
所有资料免费
|
MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
||
TD,断裂,23℃ TD, fracture, 23 ℃ |
注册或登录后
所有资料免费
|
% | ASTM D412 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
注册或登录后
所有资料免费
|
% | ISO 37 |
撕裂强度 tear strength |
注册或登录后
所有资料免费
|
||
TD,23℃ TD,23℃ |
注册或登录后
所有资料免费
|
kN/m | ISO 34-1 |
TD,23℃ TD,23℃ |
注册或登录后
所有资料免费
|
kN/m | ASTM D624 |
压缩形变 Compression deformation |
注册或登录后
所有资料免费
|
ASTM D395B | |
23℃,22 hr 23℃,22 hr |
注册或登录后
所有资料免费
|
% | ASTM D395B |
70℃,22 hr 70℃,22 hr |
注册或登录后
所有资料免费
|
% | ASTM D395B |
压缩形变 Compression deformation |
注册或登录后
所有资料免费
|
ISO 815 | |
23℃,22 hr 23℃,22 hr |
注册或登录后
所有资料免费
|
% | ISO 815 |
70℃,22 hr 70℃,22 hr |
注册或登录后
所有资料免费
|
% | ISO 815 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
注册或登录后
所有资料免费
|
||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
注册或登录后
所有资料免费
|
ISO 868 | |
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 Change in Tensile Strength |
注册或登录后
所有资料免费
|
% | ASTM D573 |
拉伸强度的变化率 Change in Tensile Strength |
注册或登录后
所有资料免费
|
% | ISO 188 |
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air |
注册或登录后
所有资料免费
|
||
100℃,168 hr 100℃,168 hr |
注册或登录后
所有资料免费
|
% | ASTM D573 |
Change in Tensile Strain at Break in Air(100℃,168 hr) Change in Tensile Strain at Break in Air(100℃,168 hr) |
注册或登录后
所有资料免费
|
% | ISO 188 |
Change in Durometer Hardness in Air(邵氏 A,100℃,672 hr) Change in Durometer Hardness in Air (100 ℃, 672 hr) |
注册或登录后
所有资料免费
|
ASTM D573 | |
空气中邵氏硬度的变化率 Change in Shore Hardness in Air |
注册或登录后
所有资料免费
|
||
邵氏 A,100℃,672 hr Shore A, 100 ℃, 672 hr |
注册或登录后
所有资料免费
|
ISO 188 | |
Change in Mass in Air(100℃,168 hr) Change in Mass in Air(100℃,168 hr) |
注册或登录后
所有资料免费
|
% | ASTM D573 |
Change in Mass in Air(100℃,168 hr) Change in Mass in Air(100℃,168 hr) |
注册或登录后
所有资料免费
|
% | ISO 188 |
Change in Volume in Air(100℃,168 hr) Change in Volume in Air(100℃,168 hr) |
注册或登录后
所有资料免费
|
% | ASTM D573 |
Change in Volume in Air(100℃,168 hr) Change in Volume in Air(100℃,168 hr) |
注册或登录后
所有资料免费
|
% | ISO 188 |
拉伸强度的变化率 Change in Tensile Strength |
注册或登录后
所有资料免费
|
ASTM D471 | |
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
拉伸强度的变化率 Change in Tensile Strength |
注册或登录后
所有资料免费
|
ISO 1817 | |
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
极限伸长率的变化率 Change in Ultimate Elongation |
注册或登录后
所有资料免费
|
ASTM D471 | |
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
断裂时拉伸应力变化 Change in tensile stress during fracture |
注册或登录后
所有资料免费
|
ISO 1817 | |
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
Change in Durometer Hardness(邵氏 A,23℃,168 hr,in Deionized Water) Change in Durometer Hardness (23 ℃, 168 hr, in Deionized Water) |
注册或登录后
所有资料免费
|
ASTM D471 | |
邵氏硬度的变化率 Change rate of Shore hardness |
注册或登录后
所有资料免费
|
||
邵氏 A,23℃,168 hr,在去离子水中 Shore A, 23 ℃, 168 hr, in deionized water |
注册或登录后
所有资料免费
|
ISO 1817 | |
质量变化率 Quality change rate |
注册或登录后
所有资料免费
|
ASTM D471 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,在相对湿度,95% 23 ℃, 168 hr, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
38℃,168 hr,在相对湿度,95% 38 ℃, 168 hr, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
质量变化率 Quality change rate |
注册或登录后
所有资料免费
|
ISO 1817 | |
23.0℃,168 hr,在相对湿度,95% 23.0 ℃, 168 hours, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23.0℃,168 hr,in Sodium Chloride,15% 23.0℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23.0℃,168 hr,in Cascade Detergent 23.0℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23.0℃,168 hr,in Sodium Hydroxide,50% 23.0℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23.0℃,168 hr,in Hydrochloric Acid,10% 23.0℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
38.0℃,168 hr,在相对湿度,95% 38.0 ℃, 168 hours, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23.0℃,168 hr,in Clorox,10% 23.0℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23.0℃,168 hr,in Ethanol,50% 23.0℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
体积变化 Volume change |
注册或登录后
所有资料免费
|
ASTM D471 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,在相对湿度,95% 23 ℃, 168 hr, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
38℃,168 hr,在相对湿度,95% 38 ℃, 168 hr, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ASTM D471 |
体积变化 Volume change |
注册或登录后
所有资料免费
|
ISO 1817 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,在相对湿度,95% 23 ℃, 168 hr, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
38℃,168 hr,在相对湿度,95% 38 ℃, 168 hr, at relative humidity of 95% |
注册或登录后
所有资料免费
|
% | ISO 1817 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部 ![]()
石化百年产业精神展演反响热烈
2021-09-01 搜料网资讯: 凝聚精神财富 激励再建新功 8月30日,由《中国化工报》社有限公司主办的中国石油和化工百年产业精神展演暨研讨会在化工号平台直播后,在广大石油和化工企业中引发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |