牌号简介 About |
---|
高性能热塑性材料,30%碳纤维增强聚醚醚酮(PEEK),半结晶,注射成型颗粒,非常容易流动,符合FDA食品接触标准,颜色为黑色。在静态或动态系统中需要更高强度时,具有更薄横截面或更长流动长度的复杂几何体。耐磨性好,摩擦系数低,热膨胀系数低。抗腐蚀环境的化学反应。 High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour black. Complex geometries with thinner cross sections or longer flow length where higher strength in a static or dynamic system is required. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
6.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
23℃ 23℃ |
45 | kJ/m² | ISO 179/1U |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
7.0 | kJ/m² | ISO 180-A |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
23℃ 23℃ |
40 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
342 | ℃ | ISO 75-2/Af |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion |
ISO 11359-2 | ||
MD:< 143℃ MD:< 143℃ |
1/℃ | ISO 11359-2 | |
MD:> 143℃ MD:> 143℃ |
1/℃ | ISO 11359-2 | |
TD:< 143℃ TD:< 143℃ |
1/℃ | ISO 11359-2 | |
TD:> 143℃ TD:> 143℃ |
1/℃ | ISO 11359-2 | |
比热 specific heat |
|||
23℃ 23℃ |
J/kg/℃ | DSC | |
导热系数 Thermal Conductivity |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D4496 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
毒性 toxicity |
NES 713 | ||
CO content CO content |
NES 713 | ||
CO2 content CO2 content |
NES 713 | ||
Total gases Total gases |
NES 713 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,125℃ Fracture, 125 ℃ |
MPa | ISO 527-2 | |
断裂,175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
断裂,225℃ Fracture, 225 ℃ |
MPa | ISO 527-2 | |
断裂,275℃ Fracture, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
225℃ 225℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
200℃ 200℃ |
MPa | ISO 604 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 Spiral flow length |
cm | 内部方法 | |
收缩率 Shrinkage |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 模具温度: 374°F, 熔体温度: 716°F |
4 1 mm |
5 380°C nozzle |
6 Onset |
7 Average |
8 Along flow |
9 1V |
【新闻资讯】查看全部 ![]()
华安瑞在医疗模具行业打破惯例
2017-11-15 专攻精密工程和高性能塑料制品的公司在大宗商品导向型的中国可能仍是少数。 对总部位于马萨诸塞州皮茨菲尔德的华安瑞模塑有限公司来说,这条路公司至今已经走了十年。 这家美国公司在武汉设有小型注塑制模工厂,最近公开了其为总部位于波士顿的 Jana Care 公司生产的验血设备的详情。 该设备可插入智能手机,将数据传输至实验室。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |