ETFE，LNP™ THERMOCOMP™ 2C003 compound对比ETFE，LNP™ THERMOCOMP™ 2X04505 compound物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ 2C003 compound 物性表 ETFE & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ THERMOCOMP™ 2X04505 compound 物性表 ETFE & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP Thermocomp 2C003是一种以含15%碳纤维的ETFE树脂为基础的化合物。这种材料的附加特性包括：导电性。也称为：lnpThermocomp化合物fp-ec-1003产品再订购名称：2c003 LNP THERMOCOMP 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-EC-1003 Product reorder name: 2C003	LNP™ THERMOCOMP™ 2X04505是一种基于ETFE树脂的化合物，含有专有填料。 LNP™ THERMOCOMP™ 2X04505 compound LNP THERMOCOMP 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-FP-E-04505 Product reorder name: 2X04505 LNP™ THERMOCOMP™ 2X04505 compound LNP THERMOCOMP 2X04505 is a compound based on Ethylene Tetrafluoroethylene Copolymer resin containing Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound PDX-FP-E-04505 Product reorder name: 2X04505

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	ETFE ETFE	ETFE ETFE
填料：	碳纤维 15	碳纤维
用途：
性能特点：	导电 Conductive	共聚物 Copolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ 2C003 compound LNP™ THERMOCOMP™ 2X04505 compound 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage % ASTM D955

收缩率(MD：24 hrs)
Shrinkage % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage % ASTM D955

收缩率(TD：24 hrs)
Shrinkage % ISO 294-4

机械性能
MECHANICAL LNP™ THERMOCOMP™ 2C003 compound LNP™ THERMOCOMP™ 2X04505 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量
Flexural Modulus MPa ISO 178

弯曲模量(--)
Flexural Modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ THERMOCOMP™ 2C003 compound LNP™ THERMOCOMP™ 2X04505 compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multiaxial Impact J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ 2C003 compound LNP™ THERMOCOMP™ 2X04505 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

加工方式

注射 LNP™ THERMOCOMP™ 2C003 compound LNP™ THERMOCOMP™ 2X04505 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 80*10*4

6 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

ETFE，LNP™ THERMOCOMP™ 2C003 compound对比ETFE，LNP™ THERMOCOMP™ 2X04505 compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别