PPA，Amodel® A-8940 HS对比PPA，AKROMID® T1 GF 40 9 black (3499)物性表,价格行情_搜料

牌号信息	Amodel® A-8940 HS 物性表 PPA & 比利时索尔维指导价格：暂无塑料库存： 4200kg	AKROMID® T1 GF 40 9 black (3499) 物性表 PPA & 德国AKRO-PLASTIC 指导价格：暂无塑料库存：缺货
牌号简介	Amodel® A-8940 HS是一种40%的玻璃纤维增强，热稳定的聚邻苯二甲酰胺（PPA），具有很高的热偏转温度和很高的拉伸强度。优良的抗蠕变性和低吸水性也是该树脂的特点。黑色：A-8940 HS BK 328 Amodel® A-8940 HS is a 40% glass-fiber-reinforced, heat-stabilized polyphthalamide (PPA) with a high heat deflection temperature and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Black: A-8940 HS BK 328	AKROMID® T1 GF 40 9 black (3499)是一种40%的玻璃纤维增强，工艺改进的聚邻苯二甲酰胺，具有很高的刚性和强度，以及耐高温和耐化学性应用，即使在高机械负荷下也具有严格的尺寸公差。 AKROMID® T1 GF 40 9 black (3499) is a 40% glass fibre reinforced, process improved polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance Applications are parts with tight dimensional tolerances even under high mechanical load.

产品描述
厂家：	比利时索尔维 Solvay	德国AKRO-PLASTIC
类别：	PPA PPA	PPA PPA
填料：	玻璃纤维 40	玻璃纤维 40
用途：	连接器,电器用具,消费品应用领域,外壳,机器/机械部件,汽车领域的应用,工业应用,金属取代,汽车电子
性能特点：	机械强度好,韧性好,尺寸稳定性好,耐高温,耐化学性,低吸湿性 Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Low moisture absorption	机械强度好,尺寸稳定性好,耐高温,耐化学性,防火阻燃等级HB Good Rigidity,Good Dimensional Stability,High Heat Resistance,Solvent resistance,HB
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water Absorption % ASTM D570

吸水率(70℃，62% RH )
Water Absorption % ISO 1110

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

收缩率(MD)
Shrinkage % ASTM D955

收缩率(MD)
Shrinkage % ISO 294-4

收缩率(TD)
Shrinkage % ASTM D955

收缩率(TD)
Shrinkage % ISO 294-4

螺旋流动长度
Spiral flow length cm Internal Method

机械性能
MECHANICAL Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(断裂，23℃)
Flexural Strength MPa ISO 178

弯曲模量
Flexural Modulus MPa ISO 178

弯曲模量(23℃)
Flexural Modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

断裂弯曲应变
Fracture bending strain % ISO 178

断裂弯曲应变(23℃)
Fracture bending strain % ISO 178

球压硬度(H 961/30)
ball-indentation hardness MPa ISO 2039-1

冲击性能
IMPACT Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength kJ/m² ISO 180/A

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180/A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

温度指数(50% 拉伸强度损失，20000 hr)
Temperature index ℃ IEC 216

温度指数(50% 拉伸强度损失，5000 hr)
Temperature index ℃ IEC 216

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/Af

热变形温度(8.0 MPa，未退火)
HDT ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ DIN EN 11357-1

熔融温度
Melting temperature ℃ ISO 11357-3

电气性能
ELECTRICAL Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数(解决方案 A)
Comparative Tracking Index V IEC 60112

阻燃性能
FLAMMABILITY Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

0.80 mm
0.80 mm UL 94

灼热丝可燃性指数(1.6 mm)
Glow Wire Flammability Index(GWFI) ℃ IEC 60695-2-12

燃烧速率(1 mm)
Burning Speed mm/min FMVSS 302

补充信息
Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位
UNIT 测试方法
TEST METHOD

灰份含量
Ash Content % ISO 1172

加工方式

注射 Amodel® A-8940 HS AKROMID® T1 GF 40 9 black (3499) 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 模具温度: 266°F, 熔体温度: 644°F, 注塑压力: 1.09E+4 psi

3 cross section of flow spiral: 7 mm x 3.5 mm

4 0.079 in/min

5 2 mm/min

6 10°C/min

7 >1 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部