PP，SABIC® PPcompound 8632对比PP，SABIC® PPcompound 5310物性表,价格行情_搜料

牌号信息	SABIC® PPcompound 8632 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货	SABIC® PPcompound 5310 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	SABIC® PPcompound 8632是一种开发级矿物填充弹性体改性聚丙烯。典型的材料特性包括良好的流动性和冲击和刚度之间的良好平衡，以及低CLTE的额外优势。典型应用包括大型和复杂的汽车外部零件，如保险杠。SABIC® PPcompound 8632是指定的汽车等级。 SABIC® PPcompound 8632 is a development grade, mineral filled elastomer modified Polypropylene. Typical material properties include combination of good flow and excellent balance between impact and stiffness withadditonal advantage of low CLTE. Typical applications include large and complex automotive exterior parts such as bumpers. SABIC® PPcompound 8632 is a designated automotive grade.	SABIC PP化合物5310是一种填充矿物的冲击改性聚丙烯TPO。这种材料结合了耐刮性和热稳定性与汽车外部风化稳定性。IMDS ID是209727767。 SABIC® PPCOMPOUND 5310 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with exterior automotive weathering stability. The IMDS ID is 209727767.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PP PP not specified	PP PP not specified
填料：	矿物	矿物
用途：	汽车防撞杆,汽车领域的应用,汽车外部零件	汽车领域的应用,汽车外部零件
性能特点：	热膨胀系数低,冲击性能好,易流动 Low CLTE,High impact resistance,Good liquidity	耐候抗UV,冲击性能好,耐刮擦,热稳定性好 Weather resistance is good,High impact resistance,High scratch resistance,Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SABIC® PPcompound 8632 SABIC® PPcompound 5310 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(24 hrs)
Shrinkage % 内部方法

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL SABIC® PPcompound 8632 SABIC® PPcompound 5310 单位
UNIT 测试方法
TEST METHOD

弯曲模量(64 mm跨距)
Flexural Modulus MPa ISO 178

弯曲模量(注塑成型)
Flexural Modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，注塑成型)
Tensile strain % ISO 527-2/1A

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，注塑成型)
tensile strength MPa ISO 527-2/1A

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(断裂，注塑成型)
tensile strength MPa ISO 527-2/1A

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(注塑成型)
Tensile modulus MPa ISO 527-2/1A

冲击性能
IMPACT SABIC® PPcompound 8632 SABIC® PPcompound 5310 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃，注塑成型)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃，注塑成型)
Izod Notched Impact strength ISO 180/1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，注塑成型)
Izod Notched Impact strength ISO 180/1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(-30℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL SABIC® PPcompound 8632 SABIC® PPcompound 5310 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

线性热膨胀系数(MD：-30~100℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~100℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度(A50)
Vicat Softening Temperature ℃ ISO 306/A50

加工方式

注射 SABIC® PPcompound 8632 SABIC® PPcompound 5310 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

备注

2 类型1A

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 80*10*4mm, Cut

4 80*10*4 mm, Cut

5 7.22 ft/sec


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注