PEI，LNP™ THERMOCOMP™ EX00781H compound对比PEI，ULTEM™ XH6050 resin物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ EX00781H compound 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存：缺货	ULTEM™ XH6050 resin 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存： 3000kg
牌号简介	LNP Thermocomp Ex00781H是一种基于含专利填料的聚醚酰亚胺的复合材料。这种材料的附加特征是：医疗保健。也称为：lnpThermocomp化合物PDX-E-00781 EES产品再订购名称：Ex00781H LNP THERMOCOMP EX00781H is a compoud based on Polyetherimide containng Proprietary Filler(s). Added feature of this material is: Healthcare. Also known as: LNP* THERMOCOMP* Compound PDX-E-00781 EES Product reorder name: EX00781H	透明热塑性聚酰亚胺（TPI）树脂。玻璃化转变温度（Tg）247°C。该树脂具有薄壁FR功能，并具有UL94V0列表。根据VDE/DIN472第815部分，树脂符合RoHS标准且无卤素。 Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. This resin has thinwall FR capability and has a UL94 V0 listing. Resin is RoHS compliant and halogen free according VDE/DIN 472 part 815.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PEI Polyetherimide	PEI Polyetherimide
填料：	其他
用途：	医疗/护理用品
性能特点：		无卤,阻燃 Halogen free,Flame Characteristics
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water Absorption %

吸水率(饱和，23℃)
Water Absorption %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage %

收缩率(MD：3.2 mm)
Shrinkage %

收缩率(TD：3.2 mm)
Shrinkage %

熔体体积流动速率(340℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(360℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(337℃，6.60kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(--)
Flexural Strength MPa ISO 178

弯曲强度(屈服，100 mm跨度)
Flexural Strength MPa ASTM D790

弯曲强度(屈服，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量(--)
Flexural Modulus MPa ISO 178

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

球压硬度(H358/30)
ball-indentation hardness MPa ISO 2039-1

冲击性能
IMPACT LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength ASTM D4812, ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal Conductivity W/m/K ASTM E1530

热变形温度(0.45 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~150℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~150℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~150℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~150℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temperature ℃ ASTM D1525，ISO 306

电气性能
ELECTRICAL LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm ASTM D149

相比漏电起痕指数
Comparative Tracking Index V IEC 60112

耗散因数(1 kHz)
Dissipation factor

耗散因数(1 MHz)
Dissipation factor

耗散因数(100 Hz)
Dissipation factor

耗散因数(50 Hz)
Dissipation factor

耗散因数(60 Hz)
Dissipation factor

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Oxygen Index % ISO 4589-2

灼热丝可燃性指数(3.2 mm)
Glow Wire Flammability Index(GWFI) ℃ IEC 60695-2-12

灼热丝起燃温度(3 mm)
Glow Wire Ignitability Temperature(GWIT) ℃ IEC 60695-2-13

光学性能
OPTICAL LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位
UNIT 测试方法
TEST METHOD

透光率(2540 µm)
Light Transmission % ASTM D1003

雾度(2540 µm)
Haze % ASTM D1003

加工方式

注射 LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

建议注射量 LNP™ THERMOCOMP™ EX00781H compound ULTEM™ XH6050 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4

8 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 0.20 in/min

4 类型 1, 0.20 in/min

5 0.051 in/min

6 0.079 in/min

7 Yield

8 0.10 in/min

9 80*10*4 sp=62mm

10 80*10*4

11 80*10*4 mm

12 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
光学性能
加工方式
注射
建议注射量
备注
返回顶部