牌号简介	lnp stat-kon re0069s化合物lnp stat-kon re0069s是基于含有30%碳纤维的尼龙66树脂的化合物。这种材料的附加特性包括：导电、阻燃、热稳定。又名：lnpstat-kon化合物rc-1006 fr-hs产品再订购名称：re0069s lnp stat-kon re0069s化合物lnp stat-kon re0069s是一种基于尼龙66树脂的化合物，含有阻燃剂、碳纤维。这种材料的附加特性包括：导电、阻燃、热稳定。也称为：lnpstat-kon化合物rc-1006 fr-hs产品再订购名称：re0069s LNP™ STAT-KON™ RE0069S compound LNP STAT-KON RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized. Also known as: LNP* STAT-KON* Compound RC-1006 FR HS Product reorder name: RE0069S LNP™ STAT-KON™ RE0069S compound LNP STAT-KON RE0069S is a compound based on Nylon 66 resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized. Also known as: LNP* STAT-KON* Compound RC-1006 FR HS Product reorder name: RE0069S	LNP Thermocomp RC006XXH是一种基于尼龙66树脂的化合物，含有30%的碳纤维。这种材料的附加功能包括：导电、保健。也称为：lnpThermocomp化合物RC-1006 HC产品再订购名称：RC006XXH LNP THERMOCOMP RC006XXH is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. Also known as: LNP* THERMOCOMP* Compound RC-1006 HC Product reorder name: RC006XXH

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PA66 PA66	PA66 PA66
填料：	碳纤维 30	碳纤维 30
用途：		医疗/护理用品
性能特点：	阻燃,热稳定性好,导电 Flame Characteristics,Heat Stabilized,Conductive	导电 Conductive
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water Absorption % ASTM D570

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage % ASTM D955

收缩率(TD：24 hrs)
Shrinkage % ASTM D955

机械性能
MECHANICAL LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位
UNIT 测试方法
TEST METHOD

弯曲应力
Flexural Stress MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量(50 mm/min)
Flexural Modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multiaxial Impact J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Af

相对温度指数(冲击)
Relative Temp Index(RTI) ℃ UL746B

相对温度指数(强度)
Relative Temp Index(RTI) ℃ UL746B

相对温度指数(电气)
Relative Temp Index(RTI) ℃ UL746B

线性热膨胀系数(MD：-30~30℃)
Coeff.of linear therm expansion 1/℃ ASTM D696

线性热膨胀系数(TD：-30~30℃)
Coeff.of linear therm expansion 1/℃ ASTM D696

电气性能
ELECTRICAL LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位
UNIT 测试方法
TEST METHOD

表面电阻率
Surface resistivity ohm ASTM D257

阻燃性能
FLAMMABILITY LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.5mm)
Flame Class Rating UL 94

加工方式

注射 LNP™ STAT-KON™ RE0069S compound LNP™ THERMOCOMP™ RC006XXH compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部

PA66，LNP™ STAT-KON™ RE0069S compound对比PA66，LNP™ THERMOCOMP™ RC006XXH compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别