PA+TPE，NYCOA Polyamide 2011对比PA+TPE，NYCOA Polyamide 1838物性表,价格行情_搜料

牌号信息	NYCOA Polyamide 2011 物性表 PA+TPE & 美国Nycoa 指导价格：暂无塑料库存：缺货	NYCOA Polyamide 1838 物性表 PA+TPE & 美国Nycoa 指导价格：暂无塑料库存：缺货
牌号简介	NYCOA 2011是一种柔性尼龙共聚物TPE，特别适用于挤出应用。它具有中等高的熔融粘度，优良的加工性能，并产生极为坚韧和有弹性的成品。NYCOA 2011被推荐用于要求易流动、特殊韧性和低吸水性的应用。尼龙6固有的高耐热性和耐化学性得以保留。NYCOA 2011提供定制的添加剂包装：热稳定剂、紫外线稳定剂、阻燃剂和/或客户颜色。典型的应用包括柔性油管和钓鱼线。 NYCOA 2011 is a flexible Nylon copolymer TPE particularly suitable for extrusion applications. It has a moderately high melt viscosity, excellent processability and yields extremely tough and resilient finished articles. NYCOA 2011 is recommended for applications that demand easy flow, exceptional toughness, and flexibility with low moisture absorption. The high thermal and chemical resistance, inherent to Nylon 6, is retained. NYCOA 2011 is available with custom additive packages: heat stabilizer, UV stabilizer, flame retardant and/or customer colors. Typical applications include flexible tubing and fishing line.	NYCOA 1838是一种柔性尼龙共聚物TPE，适用于挤出加工和注塑成型。该树脂具有良好的韧性、柔韧性和高冲击强度，同时易于加工。NYCOA 1838推荐用于需要良好韧性和耐久性的应用。典型应用包括软触摸手柄、保龄球销底座、体育用品和柔性紧固件。 NYCOA 1838 is a flexible Nylon copolymer TPE suitable for both extrusion processing and injection molding. The resin offers excellent toughness, flexibility, and high impact strength combined with easy processability. NYCOA 1838 is recommended for applications that require good toughness and durability. Typical applications include soft-touch handles, bowling pin bases, sporting goods, and flexible fasteners.

产品描述
厂家：	美国Nycoa	美国Nycoa USA Nycoa
类别：	PA+TPE PA+TPE	PA+TPE PA+TPE
填料：
用途：	单丝,渔业应用,管件	紧固件,把手,体育用品
性能特点：	耐候抗UV,易加工,韧性好,易流动,有弹性,共聚物,耐化学性,低吸湿性 Weather resistance is good,Excellent Processability,Good flexibility,Good liquidity,Elastic,Copolymer,Solvent resistance,Low moisture absorption	冲击性能好,易加工,经久耐用,共聚物,韧性好 High impact resistance,Excellent Processability,Durability,Copolymer,Good flexibility
加工条件：	挤出 Extrusion	挤出,注射成型 Extrusion,Injection Molding

技术参数

物理性能
PHYSICAL NYCOA Polyamide 2011 NYCOA Polyamide 1838 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water Absorption % ASTM D570

吸水率(饱和)
Water Absorption % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage % ASTM D955

收缩率(TD)
Shrinkage % ASTM D955

机械性能
MECHANICAL NYCOA Polyamide 2011 NYCOA Polyamide 1838 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ASTM D790

弯曲模量
Flexural Modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

冲击性能
IMPACT NYCOA Polyamide 2011 NYCOA Polyamide 1838 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Izod Notched Impact strength J/m ASTM D256

热性能
THERMAL NYCOA Polyamide 2011 NYCOA Polyamide 1838 单位
UNIT 测试方法
TEST METHOD

熔融温度
Melting temperature ℃

加工方式

注射 NYCOA Polyamide 2011 NYCOA Polyamide 1838 单位测试方法

加工熔体温度 °C

垫层 mm

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆压缩比

螺杆长径比

注射速度 NYCOA Polyamide 2011 NYCOA Polyamide 1838 单位测试方法

垫层 mm

背压 MPa

螺杆压缩比

螺杆长径比

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射