牌号信息	KumhoSunny PPO HSP8370 物性表 PPO(PPE)+PS & 上海锦湖日丽指导价格：暂无塑料库存：缺货	NORYL™ NH4050 resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	HSP8370是一种高耐热PS/PPE合金，设计用于汽车外部/内部零件。 HSP8370 is a high heat resistance PS/PPE alloy designed for automobile exterior/interior parts.	NORYL™ NH4050 resin是一种改良的PPE+PS混合物，具有良好的非氯化非溴化阻燃性、水解稳定性、耐冲击性和耐热性、良好的流动性和低比重，适用于轻型零件。这种注塑树脂可定制颜色。NORYL™ NH4050 resin可能是工业电池应用的最佳候选产品。 NORYL® NH4050 resin is a modified PPE + PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for light-weight parts. This injection-molding resin is available in custom colors. NORYL® NH4050 resin may be an excellent candidate for industrial battery applications.

产品描述
厂家：	上海锦湖日丽 KumhoSunny	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：
用途：	汽车外部零件,汽车领域的应用,电气/电子应用领域,汽车内部零件,电气元件	电池,工业应用
性能特点：	韧性好,吸水率低,耐高温,防火阻燃等级HB Good flexibility,Low or no water absorption,High Heat Resistance,HB	冲击性能好,耐水解,易流动,无卤,阻燃,耐热性好 High impact resistance,Hydrolysis stability,Good liquidity,Halogen free,Flame Characteristics,Heat Resistance, Good
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792 , ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(--)
Shrinkage % ISO 294-4

收缩率(MD)
Shrinkage % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(--)
Flexural Strength MPa ASTM D790

弯曲强度(64 mm)
Flexural Strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量(--)
Flexural Modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

弯曲模量(64 mm)
Flexural Modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(--)
tensile strength MPa ASTM D638

拉伸强度(--)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength ISO 180

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength ISO 180

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Izod Notched Impact strength J/m ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temperature ℃ ASTM D1525 10

维卡软化温度(--)
Vicat Softening Temperature ℃ ASTM D1525 6

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

电气性能
ELECTRICAL KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm IEC 60093

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注射 KumhoSunny PPO HSP8370 NORYL™ NH4050 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 4J

4 5.5J

5 120°C/h

6 标准 B (120°C/h)

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 类型 1, 2,0 in/min

4 0,051 in/min

5 0,079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部