硅酮，Mold Max® XLS II对比硅酮，OOMOO® 30物性表,价格行情_搜料

牌号信息	Mold Max® XLS II 物性表硅酮 & 美国Smooth-On 指导价格：暂无塑料库存：缺货	OOMOO® 30 物性表硅酮 & 美国Smooth-On 指导价格：暂无塑料库存：缺货
牌号简介	Mold Max® XLS II是一种Shore 30A锡催化硅橡胶，具有很低的长期收缩率。XLS II型铸模在生产中比其他硅酮的耐久性更长，当铸造化学粗糙的树脂，如环氧树脂、聚酯以及聚氨酯泡沫时。配合比为100A:10B（按重量计）。在室温下，保质期为40分钟，固化时间为24小时。Mold Max® XLS II硅胶将重现最精细的细节，适用于各种工业和艺术相关应用，包括制作生产模具、复制原型、家具、雕塑和建筑元素。Mold Max® XLS II可使用THI-VEX II添加剂增稠，用于刷涂。Mold Max® XLS II硅树脂可用于浇铸各种材料，包括混凝土、蜡、石膏、低熔点合金/金属、环氧树脂或聚酯树脂（不使用脱模剂）和聚氨酯泡沫。 Mold Max® XLS® II is a Shore 30A tin-catalyzed silicone rubber that exhibits very low long-term shrinkage. XLS® II molds last longer than other silicones in production when casting chemically harsh resins such as epoxies and polyesters as well as urethane foams. Mix ratio is 100A:10B by weight. Pot life is 40 minutes and cure time is 24 hours at room temperature. Mold Max® XLS® II silicone will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making production molds for, reproducing prototypes, furniture, sculpture and architectural elements. Mold Max® XLS® II can be thickened with THI-VEX® II additive for brush-on applications. Mold Max® XLS® II silicone can be used to cast a variety of materials including concrete, wax, gypsum, low melt alloys/metals, epoxy or polyester resins (without using a release agent) and urethane foams.	不抽真空-无刻度-使用方便。…OOMOO 25和30是易于使用的硅橡胶化合物，具有方便的一对一体积混合比（无需比例）。两者都具有低粘度，便于混合和浇注。…不需要真空脱气。两种产品均在室温下固化，收缩率可忽略不计。OOMOO® 30的使用寿命为30分钟，固化时间为6小时。oomoo 25是一个更快的版本，具有15分钟的使用寿命和75分钟的固化时间。对于新手模具制造商来说，oomoo硅酮没有很大的撕裂强度。它们适用于制作简单的一件或两件式模块模具。如果您需要高撕裂强度硅酮，建议使用Mold Max硅酮。有关Mold Max硅酮的更多信息，请访问www.smound-on.com oomoo 25&30，它适用于各种艺术相关和工业应用，包括制作用于雕塑和原型复制的一件式和两件式块状模具、铸造石膏、树脂和蜡。OOMOO硅酮也适用于电气封装和封装应用。 No Vacuuming - No Scale - Easy To Use . . . OOMOO® 25 & 30 are easy to use silicone rubber compounds that feature convenient one-to-one by volume mix ratios (no scale necessary). Both have low viscosities for easy mixing and pouring . . . vacuum degassing is not necessary. Both products cure at room temperature with negligible shrinkage. OOMOO® 30 has a 30-minute pot life, with a six-hour cure time. OOMOO® 25 is a faster version, with a 15-minute pot life and 75 minute cure time. For The Novice Mold Maker - OOMOO® silicones do not have great tear strength. They are good for making simple one- or two-piece block molds. If you require a high-tear strength silicone, Mold Max® silicones are recommended. More information on Mold Max® silicones is available at www.smooth-on.com OOMOO® 25 & 30 are suitable for a variety of art-related and industrial applications including making one and two-piece block molds for sculpture and prototype reproduction, casting plaster, resins and wax. OOMOO® silicones are also suitable for electrical potting and encapsulation applications.

产品描述
厂家：	美国Smooth-On	美国Smooth-On
类别：	硅酮硅酮	硅酮硅酮
填料：
用途：
性能特点：	收缩性低 Low contractility	低粘度 Low Viscosity
加工条件：	浇铸 casting

技术参数

物理性能
PHYSICAL Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1475

收缩率(MD)
Shrinkage % ASTM D2566

特定体积
Specific volume cm³/g ASTM D1475

机械性能
MECHANICAL Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240

弹性体
ELASTOMER Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % ASTM D412

拉伸强度(100% 应变)
tensile strength MPa ASTM D412

拉伸强度(断裂)
tensile strength MPa ASTM D412

撕裂强度
tear strength kN/m ASTM D624

电气性能
ELECTRICAL Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

介电常数(100 Hz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(100 Hz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

热固性混合粘度
Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

脱模时间
stripping time min

脱模时间(23℃)
stripping time min

补充信息
Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

工作温度
working temperature ℃

混合比
Mixing ratio

热性能
THERMAL Mold Max® XLS II OOMOO® 30 单位
UNIT 测试方法
TEST METHOD

储存稳定性
storage stability min ASTM D2471

储存稳定性(23℃)
storage stability min ASTM D2471

导热系数
Thermal Conductivity W/m/K ASTM D1461

导热系数
Thermal Conductivity W/m/K ASTM E1461

线性热膨胀系数(MD)
Coeff.of linear therm expansion 1/℃ ASTM E831

备注

1 一般属性：这些不能被视为规格。

2 B 模具

1 一般属性：这些不能被视为规格。

2 C 模具

3 Cure Time


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
弹性体
电气性能
热固性混合粘度
补充信息
热性能
加工方式
备注