HDPE，Petrothene® LR686001对比HDPE，ALCUDIA® HDPE TR-210物性表,价格行情_搜料

牌号信息	Petrothene® LR686001 物性表 HDPE & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货	ALCUDIA® HDPE TR-210 物性表 HDPE & 西班牙莱普索尔指导价格：暂无塑料库存：缺货
牌号简介	用途：油石LR68 600 1设计用于绝缘/泡沫电话单打，是一种天然的，可膨胀的，高密度聚乙烯化合物含有化学发泡剂。LR686001高度稳定，以确保在加工、烘箱老化和底座测试过程中保持oit和热稳定性。本产品含有一种加工助剂和一种金属钝化剂，以防止电缆使用时铜降解。制造技术的进步提高了化学发泡剂在LR686001中的分散性，从而在膨胀绝缘中形成了优越的多孔结构。改进的蜂窝结构可减少火花故障和提高发泡水平。 Applications: PETROTHENE LR686001 is designed for use as insulation for foam/skin telephone singles, and is a natural, expandable, high density polyethylene compound containing a chemical blowing agent. LR686001 is highly stabilized to ensure OIT retention and thermal stability during processing, oven aging, and in pedestal testing. This product contains a processing aid and a metal deactivator to prevent degradation from copper while the cable is in service. Manufacturing advancements have improved dispersion of the chemical blowing agent in LR686001, resulting in superior cellular structure in the expanded insulation. The improved cellular structure may result in decreased spark failures and increased foaming level.	Alcudia TR210是一种高密度聚乙烯，具有优异的机械性能、韧性、良好的抗环境应力开裂性能（ESCR）和抗氧化降解稳定性。该产品在高速挤压时具有优异的性能，同时电缆表面光滑。它是稳定的，以防止热降解和剪切降解，并含有金属钝化剂，以确保长期老化性能。典型应用电话单体固体绝缘。泡沫层蒙皮中的皮肤层。胶状填充电缆。Alcudia TR210可以在230°C-260°C之间的高温下挤压而不存在热降解或剪切降解的风险。最佳条件取决于应用和使用的挤出设备。当使用适当的挤压条件进行加工时，Alcudia TR210应满足以下产品和电缆规范的要求：ISO 1872 PE KHN 45D006/012 ASTM D 1248 III，A4，E9 NF C 32-060 ISM3 BS 6234，H03 VDE 0207 TEIL2 2YI1 EN 50290-2-23 EN 50288型 ALCUDIA® TR210 is a high density polyethylene developed to provide excellent mechanical properties, toughness, good environmental stress cracking resistance (ESCR) and stability against oxidative degradation. This product provides a superior performance at high-speed extrusion together with a smooth surface finish of the cable. It is stabilized to be protected from thermal and shear degradation and contains a metal deactivator to ensure long-term ageing properties. TYPICAL APPLICATIONS Solid insulation of telephone single. Skin layer in foam-skin construction. Jelly-filled cable. ALCUDIA® TR210 can be extruded at a high melt temperature between 230°C - 260°C without risk of thermal or shear degradation. The optimum conditions depend on the application and the extrusion equipment used. When processed using proper extrusion conditions, ALCUDIA® TR210 is expected to meet the requirements of the following product and cable specifications: ISO 1872 PE KHN 45D006/012 ASTM D 1248 III, A4, Grade E9 NF C 32-060 ISM3 BS 6234, Type H03 VDE 0207 Teil2 2YI1 EN 50290-2-23 EN 50288

产品描述
厂家：	荷兰利安德巴塞尔 LyondellBasell	西班牙莱普索尔 REPSOL
类别：	HDPE HDPE	HDPE HDPE
填料：
用途：	电话绝缘体,电线电缆应用	电话绝缘体,电线电缆应用
性能特点：	发泡性好,热稳定性好 Foaming performance,Heat Stabilized	韧性好,抗应力开裂 Good flexibility,High ESCR
加工条件：	挤出 Extrusion	挤出 Extrusion

技术参数

物理性能
PHYSICAL Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ISO 1183

抗环境应力开裂(F50)
ESCR hr ASTM D1693

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，模压成型)
Tensile strain % ASTM D638

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂，模压成型)
tensile strength MPa ASTM D638

热性能
THERMAL Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位
UNIT 测试方法
TEST METHOD

氧感应时间(200℃)
Oxygen sensing time min EN 728

维卡软化温度
Vicat Softening Temperature ℃ ISO 306/A

脆化温度
Brittle Temperature ℃ ASTM D746

电气性能
ELECTRICAL Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 MHz)
Dissipation factor ASTM D150

老化性能
AGING Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位
UNIT 测试方法
TEST METHOD

机械性能的保留率(100℃)
Retention rate of mechanical properties % ISO 527-3

补充信息
Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位
UNIT 测试方法
TEST METHOD

Long Term Stability
Long Term Stability IEC 60811-4-2

体重增量(by gel absorption，70℃)
Weight gain % IEC 60811-4-2

加工方式

挤出 Petrothene® LR686001 ALCUDIA® HDPE TR-210 单位测试方法

口模温度 °C

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0 Failures

3 10 days


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
电气性能
老化性能
补充信息
加工方式
挤出
备注