PC，LEXAN™ HPX4 resin对比PC，LEXAN™ EXL1413T resin物性表,价格行情_搜料

牌号信息	LEXAN™ HPX4 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ EXL1413T resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存： 5000kg
牌号简介	中流量专用聚碳酸酯-提高加工性和高压灭菌性。用于医疗设备和医药应用。卫生保健变化管理，生物相容性（ISO10993或USP六级）。ETO和蒸汽灭菌。 TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp. In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles. TROGAMID® T5000 Permanently transparent polyamide for injection molding, extrusion, and blow molding; no additives.	Lexan Exl1413t树脂Lexan Exl1413t聚碳酸酯（PC）硅氧烷共聚物树脂是一种透明的注塑级树脂。该树脂具有良好的低温（30°C）延展性，同时具有中等流动特性和良好的加工性能，与标准PC相比，具有更短的IM循环时间的机会。LEXAN™ EXL1413T resin是一种通用产品，有透明和不透明的颜色，是广泛应用的理想选择。阳离子。 LEXAN™ EXL1413T resin LEXAN EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1413T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	药物,电气/电子应用领域,医疗/护理用品,液体处理,电子显示器	通用
性能特点：	易加工,蒸汽消毒,生物兼容性,流动性中等,耐高压加热性,环氧乙烷消毒 Excellent Processability,Steam sterilized,Biocompatible,Moderate liquidity,High pressure heat resistance,Ethylene oxide disinfection	易加工,机械强度好-延展,成型周期快,流动性中等,共聚物,防火阻燃等级V-2 Excellent Processability,Ductility,Quick molding cycle,Moderate liquidity,Copolymer,V-2
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage % 内部方法

收缩率(TD：3.2 mm)
Shrinkage % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(-30℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(强度机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~95℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~95℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temperature ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

电气性能
ELECTRICAL LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

2.50 mm
2.50 mm UL 94

灼热丝可燃性指数(3.0 mm)
Glow Wire Flammability Index(GWFI) ℃ IEC 60695-2-12

灼热丝起燃温度(0.8 mm)
Glow Wire Ignitability Temperature(GWIT) ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Glow Wire Ignitability Temperature(GWIT) ℃ IEC 60695-2-13

光学性能
OPTICAL LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

透光率(2540 µm)
Light Transmission % ASTM D1003

雾度(2540 µm)
Haze % ASTM D1003

机械性能
MECHANICAL LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

洛氏硬度(L 级)
Rockwell hardness ASTM D785

洛氏硬度(L 级)
Rockwell hardness ISO 2039-2

加工方式

注射 LEXAN™ HPX4 resin LEXAN™ EXL1413T resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 10 K/min

3 100 drops value

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 80*10*4 mm

10 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
光学性能
机械性能
加工方式
注射
备注