牌号信息	Drystar™ 0601 物性表 PCTG & 美国伊士曼指导价格：暂无塑料库存：缺货	Eastman™ 1223 物性表 PCTG & 美国伊士曼指导价格：暂无塑料库存：缺货
牌号简介	Eastman很高兴宣布推出Drystar共聚酯。该新产品线是为满足变换器对共聚酯干燥要求寻求增值解决方案的需要而设计的。伊士曼？S共聚酯因其优异的美学、冲击强度和耐化学性等性能平衡而受到高度重视。当树脂按照推荐的干燥条件和设备适当脱水时，这些性能可以得到最佳的实现。认识到这一价值，Eastman构想了Drystar共聚酯，允许转换器有限地访问干燥剂烘干机，以实现这些优化。此外，一些带有干燥剂烘干机的转换器可能仍然发现Drystar共聚酯的价值增加，通过在注塑、型材挤压或挤出吹塑共聚酯之前去除干燥过程，从而获得生产灵活性和成本节约。最初的发布包括四个等级的Drystar共聚酯的商业化，Eastman正在进行计划，以在未来扩展这一战略产品线。Drystar仅在亚太地区提供。 Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment. Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future. *DRYSTAR is only available in the Asia Pacific Region.	伊斯曼共聚酯1223是一种透明的无定形材料。由于其在加工温度下的透明度、韧性和良好的熔融强度，它可用于各种加工技术，包括薄膜和片材挤压。Eastman共聚酯1223可使用颜色浓缩物、干色或液体着色剂着色。 Eastman™ copolyester 1223 is a clear, amorphous material. Because of its clarity, toughness and good melt strength at processing temperatures, it is useful in a variety of processing techniques including film and sheet extrusion. Eastman™ Copolyester 1223 may be colored using color concentrates, dry colors or liquid colorants.

产品描述
厂家：	美国伊士曼 Eastman	美国伊士曼 Eastman
类别：	PCTG PCTG	PCTG PCTG
填料：
用途：		容器,玩具,收缩性薄膜,食品包装,体育用品,文具,工业应用,消费品应用领域,层压板,家具,显示器装饰
性能特点：	表面光泽度好,冲击性能好,耐化学性 Good surface appearance,High impact resistance,Solvent resistance	透光性好,韧性好,电子束消毒,熔体强度好,辐射消毒,环氧乙烷消毒,无定形的 Good Clarity,Good flexibility,E-beam disinfection,Good melt strength,Radiation disinfection,Ethylene oxide disinfection,Amorphous
加工条件：	挤出吹塑成型

技术参数

物理性能
PHYSICAL Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water Absorption % ASTM D570，ISO 62

固有粘度(Pellets：23℃)
Intrinsic viscosity 内部方法

固有粘度(薄膜，23℃)
Intrinsic viscosity 内部方法

密度(--)
Density g/cm³ ASTM D792 , ASTM D1505

密度(23℃)
Density g/cm³ ISO 1183/D

薄膜
Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

PPT撕裂阻力(MD：23℃，250 mm)
PPT tear resistance N ASTM D2582

PPT撕裂阻力(TD：23℃，250 mm)
PPT tear resistance N ASTM D2582

二氧化碳渗透性(23℃)
Carbon dioxide permeability cm³·mm/m²/atm/24 hr ASTM D1434

二氧化碳渗透性(23℃，250.0 µm)
Carbon dioxide permeability cm³·mm/m²/atm/24 hr ASTM D1434

割线模量(MD)
Secant modulus MPa ASTM D882

割线模量(MD：250 µm)
Secant modulus MPa ASTM D882

割线模量(TD)
Secant modulus MPa ASTM D882

割线模量(TD：250 µm)
Secant modulus MPa ASTM D882

埃尔曼多夫抗撕强度(MD)
Elmandorf tear strength g ASTM D1922

埃尔曼多夫抗撕强度(MD：250 µm)
Elmandorf tear strength N ASTM D1922

埃尔曼多夫抗撕强度(TD)
Elmandorf tear strength g ASTM D1922

埃尔曼多夫抗撕强度(TD：250 µm)
Elmandorf tear strength N ASTM D1922

抗撕裂蔓延性(M.D.：23℃)
Tear resistant vine ductility kN/m ASTM D1938

抗撕裂蔓延性(Split Tear Method，MD：23℃，250 mm)
Tear resistant vine ductility kN/m ASTM D1938

抗撕裂蔓延性(Split Tear Method，TD：23℃，250 mm)
Tear resistant vine ductility kN/m ASTM D1938

抗撕裂蔓延性(T.D.：23℃)
Tear resistant vine ductility kN/m ASTM D1938

拉伸应变(MD，屈服)
Tensile strain % ASTM D882

拉伸应变(MD，屈服，250 µm)
Tensile strain % ASTM D882

拉伸应变(MD，断裂)
Tensile strain % ASTM D882

拉伸应变(MD，断裂，250 µm)
Tensile strain % ASTM D882

拉伸应变(TD，屈服)
Tensile strain % ASTM D882

拉伸应变(TD，屈服，250 µm)
Tensile strain % ASTM D882

拉伸应变(TD，断裂)
Tensile strain % ASTM D882

拉伸应变(TD，断裂，250 µm)
Tensile strain % ASTM D882

拉伸强度(MD，屈服)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，250 µm)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂)
tensile strength MPa ASTM D882

拉伸强度(MD，断裂，250 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，250 µm)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂)
tensile strength MPa ASTM D882

拉伸强度(TD，断裂，250 µm)
tensile strength MPa ASTM D882

水气透过率(38℃，100% RH)
Water vapor transmittance g/m²/24 hr ASTM F1249

水气透过率(38℃，100% RH，250 µm)
Water vapor transmittance g/m²/24 hr ASTM F1249

落锤冲击(-18℃)
Gardner Impact g ASTM D1709-A

落锤冲击(-18℃，250 µm)
Gardner Impact g ASTM D1709-A

落锤冲击(23℃)
Gardner Impact g ASTM D1709-A

落锤冲击(23℃，250 µm)
Gardner Impact g ASTM D1709-A

薄膜厚度(测试)
film thickness µm

裤型撕裂耐性(MD)
Pant tear resistance N/mm ISO 6383-1

裤型撕裂耐性(MD：250 µm)
Pant tear resistance N/mm ISO 6383-1

裤型撕裂耐性(TD)
Pant tear resistance N/mm ISO 6383-1

裤型撕裂耐性(TD：250 µm)
Pant tear resistance N/mm ISO 6383-1

透氧率(23℃)
Oxygen permeability cm³·mm/m²/atm/24 hr ASTM D3985

透氧率(23℃，250 µm，50% RH)
Oxygen permeability cm³·mm/m²/atm/24 hr ASTM D3985

冲击性能
IMPACT Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁无缺口冲击强度(-20℃，3.2 mm)
Izod Unnotched Impact strength ASTM D4812

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁无缺口冲击强度(-30℃，3.2 mm)
Izod Unnotched Impact strength ASTM D4812

悬臂梁无缺口冲击强度(-40℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁无缺口冲击强度(-40℃，3.2 mm)
Izod Unnotched Impact strength ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁无缺口冲击强度(23℃，3.2 mm)
Izod Unnotched Impact strength ASTM D4812

悬臂梁缺口冲击强度(-40℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(-40℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(-40℃，2.50 mm，Energy @ Max. Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(-40℃，2.50 mm，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(-40℃，2.50 mm，能量到力量峰值)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(-40℃，3.20 mm，Energy @ Max. Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(-40℃，3.20 mm，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(-40℃，3.20 mm，能量到力量峰值)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，2.50 mm，Energy @ Max. Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，2.50 mm，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，2.50 mm，能量到力量峰值)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，3.20 mm，Energy @ Max. Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，3.20 mm，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，3.20 mm，能量到力量峰值)
Dart impact equipped with measuring instruments J ISO 6603-2

热性能
THERMAL Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

导热系数(23℃)
Thermal Conductivity W/m/K ASTM C177

比热(100℃)
specific heat J/kg/℃ DSC

比热(150℃)
specific heat J/kg/℃ DSC

比热(200℃)
specific heat J/kg/℃ DSC

比热(250℃)
specific heat J/kg/℃ DSC

比热(60℃)
specific heat J/kg/℃ DSC

热变形温度(0.45 MPa，未退火)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
HDT ℃ ASTM D648

玻璃化转变温度
Glass transition temperature ℃ DSC

线性热膨胀系数(MD：-30~40℃)
Coeff.of linear therm expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temperature ℃ ASTM D1525

电气性能
ELECTRICAL Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

介电常数(23 ℃，1 kHz)
Dielectric constant ASTM D150

介电常数(23 ℃，1 MHz)
Dielectric constant ASTM D150

介电强度(23℃)
Dielectric strength kV/mm ASTM D149

体积电阻率(23℃)
Volume resistivity ohms·cm ASTM D257

耐电弧性
Arc resistance sec ASTM D495

耗散因数(23℃，1 kHz)
Dissipation factor ASTM D150

耗散因数(23℃，1 MHz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

光学性能
OPTICAL Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

光泽度(45°)
gloss ASTM D2457

光泽度(45°，250 µm)
gloss ASTM D2457

透光率(常规)
Light Transmission % ASTM D1003

透光率(常规，250 µm)
Light Transmission % ASTM D1003

透光率(总计)
Light Transmission % ASTM D1003

透光率(总计，250 µm)
Light Transmission % ASTM D1003

透明度
transparency ASTM D1746

雾度
Haze % ASTM D1003

雾度(250 µm)
Haze % ASTM D1003

机械性能
MECHANICAL Drystar™ 0601 Eastman™ 1223 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
Flexural Strength MPa ISO 178

弯曲强度(屈服，23℃)
Flexural Strength MPa ASTM D790

弯曲模量(23℃)
Flexural Modulus MPa ASTM D790

弯曲模量(23℃)
Flexural Modulus MPa ISO 178

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638 , ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638 , ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ASTM D638 , ISO 527-2

撕裂阻力(M.D.：23℃)
Tear resistance N ASTM D2582

撕裂阻力(T.D.：23℃)
Tear resistance N ASTM D2582

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

加工方式

注射 Drystar™ 0601 Eastman™ 1223 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 EMN-A-AC-GV-1

3 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop

4 7.9 in/min

5 50% RH

6 254 mm/min, Split Tear Method

7 4 mm

8 13.5 ft/sec, 0.79 in 冲击器直径

9 40 mm support and clamp diameter

10 500 V/sec, 方法A（短时间）

1 一般属性：这些不能被视为规格。

2 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop

3 7.9 in/min

4 4 mm

5 13.5 ft/sec, 0.79 in 冲击器直径

6 40 mm support and clamp diameter

7 500 V/sec, 方法A（短时间）


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
冲击性能
热性能
电气性能
光学性能
机械性能
加工方式
注射
备注
返回顶部

PCTG，Drystar™ 0601对比 PCTG，Eastman™ 1223对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别