PS，PRE-ELEC® PS 1324对比PS，PRE-ELEC® PS 1326物性表,价格行情_搜料

牌号信息	PRE-ELEC® PS 1324 物性表 PS & 芬兰普宓斯指导价格：暂无塑料库存：缺货	PRE-ELEC® PS 1326 物性表 PS & 芬兰普宓斯指导价格：暂无塑料库存：缺货
牌号简介	PRE-ELEC® PS 1324是一种基于聚苯乙烯的碳黑填充导电热塑性化合物。除了低电阻率。PRE-ELEC® PS 1324具有良好的机械性能平衡，易于挤压。典型应用包括热成型静电放电托盘的挤压板。 PRE-ELEC® PS 1324 is a carbon black filled conductive thermoplastic compound based on polystyrene. In addition to a low electrical resistivity. PRE-ELEC® PS 1324 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include extruded sheet for thermoformed ESD trays.	PRE-ELEC® PS 1326是一种基于聚苯乙烯的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PS 1326具有优良的机械性能，易于注射成型。典型应用包括静电放电敏感产品的注射成型手提箱和载带卷盘。 PRE-ELEC® PS 1326 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PS 1326 has excellent mechanical properties and is easy to injection mould. Typical applications include injection moulded tote bins and carrier tape reels for ESD sensitive products.

产品描述
厂家：	芬兰普宓斯 Premix Oy	芬兰普宓斯 Premix Oy
类别：	PS PS	PS PS
填料：
用途：		装货箱,容器
性能特点：	易加工,导电 Excellent Processability,Conductive	易加工,导电 Excellent Processability,Conductive
加工条件：	挤出 Extrusion	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage % ASTM D955

收缩率(MD)
Shrinkage % ISO 294-4

熔体质量流动速率(200℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，21.6kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

弯曲模量(4 mm)
Flexural Modulus MPa ASTM D790

弯曲模量(4 mm)
Flexural Modulus MPa ISO 178

拉伸应变(TD，屈服)
Tensile strain % ASTM D638

拉伸应变(TD，屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(流量，屈服)
Tensile strain % ASTM D638

拉伸应变(流量，屈服)
Tensile strain % ISO 527-2

拉伸应变(流量，断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(--)
tensile strength MPa ISO 527-2

拉伸强度(MD)
tensile strength MPa ASTM D638

拉伸强度(MD，屈服)
tensile strength MPa ASTM D638

拉伸强度(MD，屈服)
tensile strength MPa ISO 527-2

拉伸强度(TD)
tensile strength MPa ASTM D638

拉伸强度(TD，屈服)
tensile strength MPa ASTM D638

拉伸强度(TD，屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240

邵氏硬度(邵氏 A)
Shore hardness ISO 868

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Izod Unnotched Impact strength kJ/m² ISO 180

悬臂梁无缺口冲击强度(-20℃，4 mm)
Izod Unnotched Impact strength kJ/m² ASTM D256

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180

悬臂梁无缺口冲击强度(23℃，4 mm)
Izod Unnotched Impact strength kJ/m² ASTM D256

悬臂梁缺口冲击强度(-20℃)
Izod Notched Impact strength kJ/m² ISO 180

悬臂梁缺口冲击强度(-20℃，4.00 mm)
Izod Notched Impact strength kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，4.00 mm)
Izod Notched Impact strength kJ/m² ASTM D256

悬臂梁缺口冲击强度(Area)
Izod Notched Impact strength ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotched Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotched Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

Bending Test(--)
Bending Test Cycles

热变形温度(0.45 MPa，未退火)
HDT ℃ ASTM D648-B

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
HDT ℃ ASTM D648-A

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/Af

维卡软化温度(A50)
Vicat Softening Temperature ℃ ISO 306/A50

电气性能
ELECTRICAL PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

表面电阻率
Surface resistivity ohms ESD STM11.11

表面电阻率
Surface resistivity ohms IEC 61340-2-3

加工方式

挤出 PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位测试方法

干燥时间 hr

干燥温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

注射 PRE-ELEC® PS 1324 PRE-ELEC® PS 1326 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 Across Flow

3 Flow

4 4 mm thickness

5 速率 A (50°C/h), 载荷2 (50N)

6 Across Flow, ISO 5626

7 Flow, ISO 5626

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 速率 A (50°C/h), 载荷2 (50N)