PLA，AgriPlast NFNI 3070/40000 HM对比PLA，TRANSMARE® BIO 6LA-3CE00物性表,价格行情_搜料

牌号信息	AgriPlast NFNI 3070/40000 HM 物性表 PLA & 德国Biowert 指导价格：暂无塑料库存：缺货	TRANSMARE® BIO 6LA-3CE00 物性表 PLA & 荷兰Transmare 指导价格：暂无塑料库存：缺货
牌号简介	AgriPlast NFNI 3070/40000 HM由30%的纤维素纤维和70%的聚乳酸组成。Agriplast颗粒可以与任何注塑机一起使用，加工成诸如勺子、控制台、机箱、保护盖等成型部件。颗粒也可以染色成任何颜色。注射成型的理想易流动性。制造复杂模具零件的高周期时间。Agriplast比同类纤维增强复合塑料轻。无锑无卤防火。焚烧后可回收和无残渣处理。AgriPlast NFNI 3070/40000 HM的加工说明：在70°C下充分干燥，加热区170°C降至130°C，可能的短期峰值熔化温度180°C，成型温度15-25°C，避免摩擦和剪切热，确保工具通风良好。 AgriPlast NFNI 3070/40000 HM is made up of 30% cellulose fibres obtained from meadow grass and 70% PLA (polylactic acid). AgriPlast granules can be used with any injection moulding machine and processed into moulded components such as spoons, consoles, machine cases, protective caps, etc. The granules can also be dyed any colour. Ideal ease of flow for injection moulding. High cycle times when manufacturing complex moulded parts. AgriPlast is lighter than comparable fibre-reinforced composite plastics. Fire protection without antimony and halogen. Recyclable and residue-free disposal when incinerated. Processing Notes for AgriPlast NFNI 3070/40000 HM: sufficiently dry at 70 °C, heating zones of 170 °C decreasing to 130 °C, possible short-term peak melting temperature of 180 °C, moulding temperature of 15 - 25 °C, avoid frictional and shearing heat, make sure the tool is well ventilated.	TRANSMARE® BIO 6LA-3CE00是一种以聚乳酸-英戈为基础的扩链生物聚合物。 TRANSMARE® BIO 6LA-3CE00 is a chain extended PLA INGEO™ based biopolymer.

产品描述
厂家：	德国Biowert	荷兰Transmare
类别：	PLA PLA	PLA PLA
填料：
用途：	通用,一次性餐具,外壳,护罩
性能特点：	可回收,易流动,无卤,阻燃,无锑 Renewable resources,Good liquidity,Halogen free,Flame Characteristics,No antimony	可回收 Renewable resources
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL AgriPlast NFNI 3070/40000 HM TRANSMARE® BIO 6LA-3CE00 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL AgriPlast NFNI 3070/40000 HM TRANSMARE® BIO 6LA-3CE00 单位
UNIT 测试方法
TEST METHOD

Tensile Strain at Tensile Strength
Tensile Strain at Tensile Strength % ISO 527-2

弯曲应变
Flexural Strain % ISO 178

弯曲强度
Flexural Strength MPa ISO 178

弯曲强度(注塑成型)
Flexural Strength MPa ISO 178

弯曲模量
Flexural Modulus MPa ISO 178

弯曲模量(注塑成型)
Flexural Modulus MPa ISO 178

拉伸应变(屈服，4 mm，注塑成型)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，4 mm，注塑成型)
Tensile strain % ISO 527-2/50

拉伸强度
tensile strength MPa ISO 527-2

拉伸强度(屈服，4 mm，注塑成型)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂，4 mm，注塑成型)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(4 mm，注塑成型)
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 D，注塑成型)
Shore hardness ISO 868

冲击性能
IMPACT AgriPlast NFNI 3070/40000 HM TRANSMARE® BIO 6LA-3CE00 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-40℃，注塑成型)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃，注塑成型)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-40℃，注塑成型)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，注塑成型)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁无缺口冲击强度
Charpy Unnotched Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-40℃，注塑成型)
Charpy Unnotched Impact strength kJ/m² ISO 179/1U

简支梁无缺口冲击强度(23℃，注塑成型)
Charpy Unnotched Impact strength kJ/m² ISO 179/1U

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-40℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

热性能
THERMAL AgriPlast NFNI 3070/40000 HM TRANSMARE® BIO 6LA-3CE00 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temperature ℃ ISO 306/A

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

加工方式

注射 AgriPlast NFNI 3070/40000 HM TRANSMARE® BIO 6LA-3CE00 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 3-point bending


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部