| Eastman很高兴宣布推出Drystar*共聚酯。该新产品线是为满足变换器对共聚酯干燥要求寻求增值解决方案的需要而设计的。伊士曼？S共聚酯因其优异的美学、冲击强度和耐化学性等性能平衡而受到高度重视。当树脂按照推荐的干燥条件和设备适当脱水时，这些性能可以得到最佳的实现。认识到这一价值，Eastman构想了Drystar共聚酯，允许转换器有限地访问干燥剂烘干机，以实现这些优化。此外，一些带有干燥剂烘干机的转换器可能仍然发现Drystar共聚酯的价值增加，通过在注塑、型材挤压或挤出吹塑共聚酯之前去除干燥过程，从而获得生产灵活性和成本节约。最初的发布包括四个等级的Drystar共聚酯的商业化，Eastman正在进行计划，以在未来扩展这一战略产品线。*Drystar仅在亚太地区提供。 Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment. Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future. *DRYSTAR is only available in the Asia Pacific Region. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 耐化学性; 冲击性能好; 表面光泽度好; Good surface appearance,High impact resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.27 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage |
|||
|
MD：3.2 mm MD：3.2 mm |
0.20 到 0.50 | % | ASTM D955 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
|
-40℃ -40℃ |
40 | J/m | ASTM D256 |
|
23℃ 23℃ |
110 | J/m | ASTM D256 |
|
-40℃ -40℃ |
4.4 | kJ/m² | ISO 180 |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
ASTM D256 | ||
|
-40℃ -40℃ |
ASTM D256 | ||
|
23℃ 23℃ |
ASTM D256 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648，ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648，ISO 75-2/A | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Light Transmission |
|||
|
总计 total |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D638 | |
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Flexural Modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 Flexural Strength |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
扬子石化消弭乙烯压缩机运转难题
2016-09-13 “现在乙烯裂解气压缩机的运行效率提高了，节能效果很明显!”9月7日，扬子石化烯烃厂设备管理科设备员石祥利说，该公司近日通过技术攻关，成功消除了乙烯裂解气压缩机透平真空度不达标的运行难题，提高了压缩机的运行效率，降低了能耗。 由于长周期运行等原因，扬子石化乙烯裂解气压缩机透平真空度不达标，效率较低，能耗较高。为此，扬子石化机动部牵头，专门成立了攻关小组，开展技术攻关。首先，该公司邀请检测单位，利用超声波检漏仪，专门对压缩机透平进行检测和查漏，消除漏点。为了彻底解决运行难题，扬 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付