| 牌号简介 About |
|---|
| EP158是一种通用尼龙66树脂。该树脂具有高强度、高韧性、高冲击性、良好的表面润滑性、耐磨性、耐低温、自熄性等工程性能，具有良好的平衡组合。典型应用EP158适用于复合和注塑成型，也广泛用于单丝、短纤维的纺纱。终端主要应用于机械、电子、电气、仪表、汽车零部件、铁路、家电、通信、纺织、油管/油罐及精密工程产品等，也可用于生产薄膜、包装、医疗设备、体育用品、日用品等。 EP158 is a general purpose Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength: good toughness; high impact; good surface lubricity: abrasion resistance; resistant low temperature: self-extinguishment. Typical Applications EP158 is suitable for compounding and injection molding, also widely used in spinning monofilament, staple. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances, communications, textile, oil pipe/tank and precision engineering products, etc., EP158 also can be used for the production of film, packing, medical equipment, sporting goods, and daily necessities and so on. |
产品描述 Product Description
用途：薄膜;电气/电子应用领域;医疗器械;体育用品;纺织应用;单丝;水箱;电器用具;通讯器材;工程配件;汽车领域的应用;包装;通用;复合;管道系统;
颜色：清晰/透明
加工条件：复合
性能特点： 机械强度好; 耐磨; 耐低温; 自熄; 冲击性能好; 韧性好; Good Rigidity,Good flexibility,High impact resistance,Antifreeze,Self-extinguishing,Good wear resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.13-1.14 | g/cm³ | ISO 1183 |
|
吸水率 Water Absorption |
|||
|
23℃，24hr 23℃，24hr |
0.04 | % | ISO 62 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
275℃，2.16kg 275℃，2.16kg |
70 | g/10min | ISO 1133 |
|
端氨基 Terminal amino group |
41±5 | Meq/Kg-NH 2 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
23℃ 23℃ |
75 | MPa | ISO 527-2 |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
弯曲强度 Flexural Strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲模量 Flexural Modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
维卡软化温度 Vicat Softening Temperature |
|||
|
A120 A120 |
℃ | ISO 306/A50 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating |
|||
|
1.00mm 1.00mm |
UL 94 | ||
|
3.00mm 3.00mm |
UL 94 | ||
|
0.70mm 0.70mm |
UL 94 | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 48h/23°C/50%RH |
| 3 10°C/min |
|
【新闻资讯】查看全部 
意大利CRP集团研发3D打印资料Windform
2016-05-18 3D打印存在着许多不同的技术，它们的不同之处在于以可用的材料的方式，并以不同层构建创建部件。 意大利CRP集团研发3D打印材料Windform 意 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付