| 牌号简介 About |
|---|
| EMERGE™ PC/PET 9100CR高级树脂是一种具有优异耐化学性的聚碳酸酯混合物。该等级设计用于医疗设备外壳，可承受反复接触医院常用的各种清洁剂和消毒剂。该等级具有良好的美观性和韧性。主要特点：根据ISO 10993 UL标准对HB应用进行了耐化学性测试：医疗器械外壳或外壳 EMERGE™ PC/PET 9100CR advanced resin is a polycarbonate blend with excellent chemical resistance. This grade was designed for use in medical equipment housings and can withstand repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. Main Characteristics: Excellent chemical resistance Tested under ISO 10993 UL listing for HB Applications: Medical device housings or enclosures |
产品描述 Product Description
用途：医疗/护理用品;电器外壳;外壳;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 耐化学性; 生物兼容性; 韧性好; 表面光泽度好; Good flexibility,Good surface appearance,Biocompatible,Solvent resistance,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.23 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，5.0kg 260℃，5.0kg |
8.5 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage |
ASTM D955 | ||
|
MD MD |
0.60 到 0.90 | % | ASTM D955 |
|
TD TD |
0.50 到 0.80 | % | ASTM D955 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ASTM D256 | ||
|
-30℃，3.2mm，注塑成型 -30 ℃, 3.2mm, injection molding |
750 | J/m | ASTM D256 |
|
23℃，3.2mm，注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
|
-40℃，3.20 mm，注塑，Peak Energy -40 ℃, 3.20 mm, injection molded, Peak Energy |
J | ASTM D3763 | |
|
-40℃，3.20 mm，注塑，Total Energy -40 ℃, 3.20 mm, injection molded, Total Energy |
J | ASTM D3763 | |
|
23℃，3.20 mm，注塑，Peak Energy 23 ℃, 3.20 mm, injection molded, Peak Energy |
J | ASTM D3763 | |
|
23℃，3.20 mm，注塑，总能量 23 ℃, 3.20 mm, injection molding, total energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 7 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
IEC 60243-1 | ||
|
1.6 mm，在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.00 mm 1.00 mm 8 |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级，3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
|
拉伸模量 Tensile modulus 4 |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded 4 |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 5 |
ASTM D638 | ||
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
MPa | ASTM D638 | |
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 5 |
ASTM D638 | ||
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus 6 |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded 6 |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength 6 |
|||
|
3.20 mm，注塑成型 3.20 mm, injection molded 6 |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
| 2 一般属性：这些不能被视为规格。 |
| 3 0,20 in/min |
| 4 2,0 in/min |
| 5 0,051 in/min |
| 6 标准 B (120°C/h), 压 力1 (10N) |
| 7 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
|
【新闻资讯】查看全部
中国化工收购克劳斯玛菲集团完成交割！
2016-05-04 近日，中国化工集团公司(“中国化工”)完成收购德国克劳斯玛菲集团的交割。该交易已获得所有监管部门的批准。未来，在运营和管理相关机械企业方面，克劳斯玛菲集团将成为中国化工集团公司的主体企业，借助于双方的实力，公司将进一步开发并参与国际市场的竞争。 提升中国化工的先进制造板块 中国化工集团公司董事长任建新表示：“克劳斯玛菲集团将给中国化工先进制造板块注入强劲的‘德国工业4.0’基因和具有制造业传统的‘工匠精神’，为全球更多客户，尤其是新兴市场，提供全面解决方案， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付