| 牌号简介 About |
|---|
| Reon 67-01是一种中等分子量悬浮型聚氯乙烯树脂，适用于硬质挤出制品。特别推荐用于刚性管道、刚性型材、刚性片材、未增塑管膜等，其中等分子量与高表观体积密度的结合使其适用于高输出率的易加工，同时保持高机械性能。它的平衡热损失特性不允许静电的发展和减少流动时间。同时，树脂所含挥发物最少。窄的孔隙范围Reon 67-01使其易于在恒定的润滑剂水平上保持均匀的熔点。该树脂颗粒的均匀粗糙度使其易于批量搬运，对润滑剂的要求最低，在挤出机中的助熔剂更均匀。 Reon 67-01 is a medium molecular weight suspension type PVC resin suitable for rigid extrusion products. It is specially recommended for rigid pipes & conduits, rigid profiles, rigid sheets, unplasticised tubular film etc. Its combination of medium molecular weight with high apparent bulk density makes it suitable for easy processing at high output rate, still maintaining the high mechanical properties. Its balanced heat loss property does not allow static to develop and reduces the flow time. At the same time the resin contains minimum volatiles. The narrow range of porosity of Reon 67-01 makes it easy to maintain a uniform fusion point at constant lubricant level. Uniform coarseness of the grains of this resin results in easy bulk handling, minimum requirement of lubricant and more uniform fluxing in the extruder. |
产品描述 Product Description
用途：薄膜;片材;型材;导管;管道系统;
颜色：清晰/透明
加工条件：挤出 Extrusion
性能特点： 均聚物; 易加工; Excellent Processability,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表观密度 Apparent density |
0.55 | g/cm³ | ASTM D1895 |
|
K-Value K-Value 2 |
67.0 | ||
|
固有粘度 Intrinsic viscosity |
0.92 | ASTM D1243 | |
|
颗粒大小分布 Particle size distribution |
ASTM D1921 | ||
|
Retention on ASTM 40 mesh Retention on ASTM 40 mesh |
< 0.10 | % | ASTM D1921 |
|
Retention on ASTM 60 mesh Retention on ASTM 60 mesh |
< 5.0 | % | ASTM D1921 |
|
Through ASTM 140 mesh Through ASTM 140 mesh |
% | ASTM D1921 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热损耗 Heat loss |
% | ASTM D3030 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Dark Resin（for 100 g resin） Dark Resin（for 100 g resin） |
count/g | ||
|
Residual Vinyl Chloride Monomer Residual Vinyl Chloride Monomer |
ppm | ASTM D3749 | |
|
孔隙度 porosity |
|||
|
DOP DOP |
cm³/g | ASTM D3367 | |
|
流动时间 Flow time |
sec | ASTM D1895 | |
| 备注 |
|---|
| 2 @ 1% in cyclohexanone |
|
【新闻资讯】查看全部
根据阻燃改性的特点制备聚丙烯泡沫
2019-03-01 聚丙烯(PP)是一种易燃材料，对聚丙烯进行阻燃改性尤为重要。近日，中科院宁波材料所郑文革研究员团队在制备高阻燃性能聚丙烯材料的基础上，采用超临界二氧化碳发泡技术协同单向牵伸法，制备出超轻、超强、高阻燃的聚丙烯泡沫。 该团队制备的聚丙烯泡沫结构独特，具有明显的各向异性。聚丙烯泡沫的密度仅为0.08g/cm3，但可支撑自重约30000倍的砝码，其比强度高达1813MPa/g・cm3，远超已知文献报道的聚合物泡沫。 不仅如此，这种聚丙烯泡沫因采用分散均匀的膨胀型阻 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付