牌号简介 About |
---|
D/W 212是一种用纯聚四氟乙烯(PTFE)刮削而成的薄膜,该薄膜一面用萘钠蚀刻。这种表面处理可以使聚四氟乙烯(通常表现出很差的粘附力)与其他材料结合。钠蚀聚四氟乙烯的主要应用包括与弹性体粘合以生产层压隔膜,以及在聚四氟乙烯压敏带生产中应用压敏粘合剂。在上述所有应用中,层压或粘合应用通常通过特定于所应用材料的底漆完成。 D/W 212 is a film , skived from virgin PTFE, that has been etched on one side with sodium naphthalene. This surface treatment allows PTFE, which normally exhibits very poor adhesion, to be bonded to other materials. The major applications for sodium etched PTFE involve bonding to elastomers to produce laminated diaphragms, as well as the application of pressure sensitive adhesives in the production of PTFE pressure sensitive tapes. In all the above applications, the lamination or adhesive application is usually accomplished with a primer that is specific to the material being applied. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thickness Thickness |
50.8 到 1020 | nm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
27.6 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
300 | % | ASTM D882 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
连续使用温度 Continuous use temperature |
260 | ℃ | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Core ID Core ID |
7.62 | cm | |
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
10亿美元天价索赔?长赐号搁浅6天后脱困,埃及当局寻求赔偿
2021-04-02 搜料网资讯: 埃及当局正为帮助长赐号(Ever Given)集装箱船从苏伊士运河脱浅寻求超过10亿美元的赔偿,而应该由谁来买单的问题尚属两难。 当地时间周三晚上,埃及国有的苏伊士运河 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |