牌号简介 About |
---|
lexan*slx2776t树脂是一种超低粘度聚碳酸酯共聚物混合物,具有增强的紫外线稳定性。此等级包含额外的脱模剂,可提供透明和着色颜色。 LEXAN* SLX2776T resin is a extra low viscosity polycarbonate copolymer blend with enhanced UV stablization. This grade contains extra mold release and is available in transparent and tinted colors |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
30 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
27.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
0.50 到 0.80 | % | 内部方法 |
吸水率 Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
0.35 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus |
|||
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 6 |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
-- -- 6 , 7 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotched Impact strength 8 |
|||
23℃ 23℃ 8 |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃,2mm 23℃,2mm |
J/m | ASTM D256 | |
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength 9 |
|||
23℃ 23℃ 9 |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 10 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temperature |
|||
-- -- |
℃ | ASTM D1525 11 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40℃ TD:-40℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
2. 5.0 mm/min |
3. 50 mm/min |
4. 类型 1, 50 mm/min |
5. 1.3 mm/min |
6. 2.0 mm/min |
7. at Yield |
8. 80*10*3 sp=62mm |
9. 80*10*3 mm |
10. 80*10*4 mm |
11. 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部 ![]()
广信材料收问询函:要求说明油墨业务毛利率下滑原因
2022-05-28 5月25日,深交所向广信材料发出年报问询函,称公司主营业务为 油墨 、涂料等电子化学品的研发、生产和销售,报告期油墨产品实现营业收入同比增长27.23%,毛利率同比下降7.05个百分 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |