| 牌号简介 About |
|---|
| Westlake ELEVATE™ EF524是一种乙烯-醋酸乙烯酯共聚物，含14.5%的VA。EF524适用于吹塑和浇铸薄膜，要求良好的光学性能和低热封性。高熔融强度使EF524成为需要高VA含量的型材挤压、成型和发泡应用的最佳选择。应用/用途：软包装薄膜可剥离密封、粘合层注射和吹塑型材挤出、管道、电线和电缆 Westlake ELEVATE™ EF524 is an ethylene vinyl acetate copolymer with 14.5% VA. EF524 is designed for blown and cast filmsrequiring excellent optics and low heat seal initiation. High melt strength makes EF524 an excellent choice for profile extrusions, molding, and foaming applications requiring high VA content. Application/Uses: Flexible packaging films Peelable seals, adhesive layers Injection and blow molding Profile extrusions, tubing, wire & cable |
产品描述 Product Description
用途：薄膜;包装;电线电缆应用;流延薄膜;型材;泡沫;吹塑成型应用;粘合剂;管件;
加工条件：流延薄膜
性能特点： 熔体强度好; 共聚物; 光学性能; 热封性好; Good heat sealing,Optical performance,Good melt strength,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.934 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
3.5 | g/10min | ASTM D1238 |
|
醋酸乙烯含量 Vinyl acetate content |
14.5 | wt% | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
51 | µm | |
|
割线模量 Secant modulus 2 |
|||
|
1% 正割，TD，51 µm，吹塑薄膜 1% secant, TD, 51 µ m, blow molded film 2 |
55.2 | MPa | ASTM D882 |
|
1% 正割，MD，51 µm，吹塑薄膜 1% secant, MD, 51 µ m, blow molded film 2 |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength 2 |
|||
|
TD，断裂，51 µm，吹塑薄膜 TD, fracture, 51 µ m, blow molded film 2 |
MPa | ASTM D882 | |
|
MD，断裂，51 µm，吹塑薄膜 MD, fracture, 51 µ m, blow molded film 2 |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain 2 |
|||
|
TD，断裂，51 µm，吹塑薄膜 TD, fracture, 51 µ m, blow molded film 2 |
% | ASTM D882 | |
|
MD，断裂，51 µm，吹塑薄膜 MD, fracture, 51 µ m, blow molded film 2 |
% | ASTM D882 | |
|
落锤冲击 Gardner Impact 2 |
|||
|
51 µm，吹塑薄膜 51 µ m, blow molded film 2 |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss 3 |
|||
|
45°，50.8 µm，吹塑薄膜 45 °, 50.8 µ m, blow molded film 3 |
ASTM D2457 | ||
|
雾度 Haze 3 |
|||
|
50.8 µm，吹塑薄膜 50.8 µ m, blow molded film 3 |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blown Film Melt Temperature Blown Film Melt Temperature |
℃ | ||
|
|
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Test run at 23°C (73°F) and 50% relative humidity |
| 3 As measured on AA formulation which contains no slip and no antiblock. |
|
【新闻资讯】查看全部 
利安德巴塞尔关闭俄罗斯办事处！此前负责在当地销售聚合物，共18名员
2022-05-12 2022年3月，美国聚烯烃集团 利安德巴塞尔 表示，在俄罗斯军队入侵乌克兰后，该公司将结束在俄罗斯的业务活动。现在该公司明确计划关闭其在莫斯科和 Togliatti的两个销售办事处， 此 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付