牌号简介 About |
---|
NORYL™ hna033树脂是一种未填充改性聚苯醚树脂,设计用于承受高压釜中的几个循环。该树脂适用于多种转换路线,可定制颜色。NORYL™ hna033树脂是一种很好的材料,适用于需要多次灭菌循环的应用。根据ISO 10993(颜色依赖性),NORYL™ HNA033树脂具有生物相容性。 NORYL HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in custom colors. NORYL HNA033 resin may be an excellent material candidate for applications requiring multiple sterilization cycles. NORYL HNA033 resin is biocompatible per ISO 10993 (color dependent). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,5.0kg 300℃,5.0kg |
8.3 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,5 kg 300℃,5 kg |
8.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
0.70 到 0.90 | % | 内部方法 |
吸水率 Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
0.15 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
-- -- 5 , 6 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 8 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 8 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temperature |
|||
-- -- |
℃ | ASTM D1525 9 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40℃ TD:-40℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
2. 5.0 mm/min |
3. 类型 1, 50 mm/min |
4. 1.3 mm/min |
5. 2.0 mm/min |
6. at Yield |
7. 80*10*4 sp=62mm |
8. 80*10*4 mm |
9. 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部 ![]()
美国总统拜登:任何年收入超过40万美元的人都将面临增税
2021-03-18 搜料网资讯: 3月17日周三,美国总统拜登表示,任何年收入超过40万美元的人都将面临增税。 此前白宫经济顾问16日表示,总统拜登的税改计划将对企业和富人加税。如果税改通过,这 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |