牌号简介 About |
---|
lnp*colorcomp*144c是一种基于聚碳酸酯的化合物。该等级的附加功能包括:UL等级HB,当需要V-2等级时推荐200系列,10.5 mfr,FDA食品接触有限颜色。自2007年1月15日起,该等级将不再支持生物相容性信息,不应用于需要生物相容性的医疗应用。 LNP* COLORCOMP* 144C is a compound based on Polycarbonate. Added features of t his grade include: UL rated HB, 200 series recommended when V-2 rating required, 10.5 MFR, FDA food contact compliant in limited colors. Effective January 15, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.20 | g/cm³ | ASTM D792 |
-- -- |
1.19 | g/cm³ | ISO 1183 , ASTM D792 |
特定体积 Specific volume |
0.830 | cm³/g | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
11 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
10.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water Absorption |
|||
24hr 24hr |
% | ASTM D570 | |
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
平衡,100℃ Equilibrium, 100 ℃ |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength 9 |
|||
23℃ 23℃ 9 |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 10 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 10 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
落锤冲击 Gardner Impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
拉伸冲击强度 Tensile impact strength 11 |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 12 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temperature |
|||
-- -- |
℃ | ASTM D1525 13 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831,ISO 11359-2 | |
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831,ISO 11359-2 | |
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal Conductivity |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 ELECTRICAL |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Comparative Tracking Index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High Voltage Arc Track Rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
1.50 mm 1.50 mm |
UL 94 | ||
极限氧指数 Oxygen Index |
% | ASTM D2863 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Light Transmission |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 4 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 5 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
-- -- 7 , 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 6 |
MPa | ASTM D790 | |
泰伯耐磨性 Taber Abrasion |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 |
备注 |
---|
3 Limited colors |
4 50 mm/min |
5 类型 1, 50 mm/min |
6 1.3 mm/min |
7 2.0 mm/min |
8 Yield |
9 80*10*4 sp=62mm |
10 80*10*4 |
11 Type S |
12 120*10*4 mm |
13 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
两岸最大石化产业合资协作项目落地福建
2017-12-27 年终岁首之际,两岸最大石化产业合资合作项目――漳州古雷炼化一体化项目落地福建。26日,十届全国人大常委会副委员长、两岸企业家峰会大陆方面副理事长盛华仁,省委书记、省长于伟国,中国石化集团公司总经理戴厚良一行来到漳州古雷炼化一体化项目建设现场,实地检查推进项目建设。盛华仁认真听取了项目负责人关于项目建设进展情况的汇报,详细询问项目规划、设计、施工等环节,要求各方精诚合作、快马加鞭、科学组织、精细管理,推动项目早日建成开始投产,把漳州古雷打造成为“技术一流、产品一流、人才一流、管理一流、效益一 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |