| 牌号简介 About |
|---|
| Clyrell RC213M Clyrell RC213M是一种α-烯烃改性聚丙烯无规共聚物，专为流延膜技术而设计。它具有极好的透明度和光泽、极低的雾度、宽的热粘范围和120°C的低密封起始温度。它设计用于高质量的包装应用，无论是作为单层膜还是作为共挤结构中的焊接层，尤其适用于印刷和金属化目的。Clyrell RC213M易于在商用铸膜设备上加工。它含有抗阻塞添加剂。Clyrell RC213M适用于食品接触，CLYRELL RC213M聚丙烯无规共聚树脂用于共挤表皮层，具有优良的光学性能，热粘范围宽，密封温度低的应用：共挤铸膜表皮层。 Clyrell RC213M Clyrell RC213M is a high flow and highly modified polypropylene random copolymer. It contains anti-blocking additives. It does not contain Calcium Stearate. Clyrell RC213M is typically used by customers for manufacturing of oriented and un-oriented films. Typical applications reported by customers are lamination, metallized films, textile and packaging of foodstuffs. In addition, customers also reported that it is particularly suitable as a skin of multilayer twist film. Customers have been reporting that films produced using Clyrell RC213M offer a good balance of properties such as high clarity, brightness, stiffness and medium seal initiation temperature (SIT). Clyrell RC213M Polypropylene Random Copolymer Resin for Skin-layer of Co-extrusion Features: Excellent optical properties Wide hot tack range Low sealing temperature Applications: Skin layer of co-extruded cast film |
产品描述 Product Description
用途：薄膜;多层薄膜;包装;流延薄膜;
加工条件：流延薄膜
性能特点： 抗结块性; 耐低温热封性; 透光性好; 无规共聚物; 食品接触; 表面光泽度好; 光学性能; 热封性好; 易加工; Excellent Processability,Good Clarity,Good surface appearance,Good heat sealing,Optical performance,High anti-blocking,Food contact compliance,Random copolymer,Low temperature heat sealing
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
10 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus 2 |
|||
|
MD，50 µm，铸造薄膜 MD, 50 µ m, cast thin film 2 |
660 | MPa | ASTM D882 |
|
拉伸强度 tensile strength 3 |
ASTM D882 | ||
|
MD，屈服，50 µm，挤塑薄膜 MD, yield, 50 µ m, extruded film |
22.0 | MPa | ASTM D882 |
|
MD，断裂，50 µm，挤塑薄膜 MD, fracture, 50 µ m, extruded film |
35.0 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
|
MD，屈服，50 µm，挤塑薄膜 MD, yield, 50 µ m, extruded film |
% | ASTM D882 | |
|
MD，断裂，50 µm，挤塑薄膜 MD, fracture, 50 µ m, extruded film |
% | ASTM D882 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temperature |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
50 µm，铸造薄膜 50 µ m, cast thin film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
ISO 527-2/50 | ||
|
屈服 yield |
% | ISO 527-2/50 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
摩擦系数 Frictional coefficient |
ASTM D1894 | ||
|
与自身 - 动态，铸造薄膜 With oneself - dynamic, casting thin films |
ASTM D1894 | ||
|
与自身 - 静态，铸造薄膜 Compared to itself - static, cast thin films |
ASTM D1894 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0,98 in/min |
| 3 20 in/min |
| 4 压 力1 (10N) |
|
【新闻资讯】查看全部 
市场准入负面清单（2022年版）公布
2022-03-25 近日，国家发展改革委 商务部公布了 市场准入负面清单（2022年版） 。 市场准入负面清单包括禁止准入类和许可准入类两大类。对市场准入负面清单以外的行业、领域、业务等，各类 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付