| 牌号简介 About |
|---|
| Westlake ELEVATE™ EF528AA是一种乙烯-醋酸乙烯酯共聚物，18.5%VA。EF528AA设计用于吹塑和浇铸薄膜，需要优良的光学性能和低热封启动。高熔融强度使EF528A成为需要中等VA含量的型材挤压、成型和发泡应用的最佳选择。应用/用途：软包装薄膜可剥密封、粘合层注塑和吹塑型材挤出、管材、电线电缆注：*AA配方不含滑脱和防堵塞。 Westlake ELEVATE™ EF528AA is an ethylene vinyl acetate copolymer with 18.5% VA. EF528AA is designed for blown and cast films requiring excellent optics and low heat seal initiation. High melt strength makes EF528AA an excellent choice for profile extrusions, molding, and foaming applications requiring medium VA content. Application/Uses: Flexible packaging films Peelable seals, adhesive layers Injection and blow molding Profile extrusions, tubing, wire & cable Note: *AA formulation contains no slip and no antiblock. |
产品描述 Product Description
用途：薄膜;包装;电线电缆应用;流延薄膜;型材;泡沫;粘合剂;管件;
加工条件：流延薄膜
性能特点： 耐低温热封性; 熔体强度好; 共聚物; 光学性能; 热封性好; Good heat sealing,Optical performance,Good melt strength,Copolymer,Low temperature heat sealing
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
2.5 | g/10min | ASTM D1238 |
|
醋酸乙烯含量 Vinyl acetate content |
18.5 | wt% | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
32 | µm | |
|
割线模量 Secant modulus |
|||
|
1% 正割，TD，32 µm，吹塑薄膜 1% 正割，TD，32 µm，吹塑薄膜 |
50.3 | MPa | ASTM D882 |
|
1% 正割，MD，32 µm，吹塑薄膜 1% secant, MD, 32 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，32 µm，吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
MPa | ASTM D638 | |
|
MD，断裂，32 µm，吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，32 µm，吹塑薄膜 TD, fracture, 32 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，32 µm，吹塑薄膜 MD, fracture, 32 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Gardner Impact |
|||
|
32 µm，吹塑薄膜 32 µ m, blow molded film |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，31.8 µm，吹塑薄膜 45 °, 31.8 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
31.8 µm，吹塑薄膜 31.8 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blown Film Melt Temperature Blown Film Melt Temperature |
℃ | ||
|
|
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
扬大高吸水性树脂抗菌关键技术研讨获重要打破
2015-12-31 记者日前从扬州大学化学化工学院获悉，由该校朱爱萍教授主持的抗菌性高吸水性树脂研制，关键技术研究取得重要突破，将纳米银成功地均匀结合在高吸水性树脂表面。 朱爱萍介绍，纳米级银系抗菌剂的抗菌机理是: 银离子与细菌接触后，到达微生物细胞壁，带正电荷的银离子吸附在带负电荷的细胞壁上，依靠库仑力使两者牢固吸附。银离子穿透细胞壁进入细胞内，与-SH基反应，使蛋白质凝固，使微生物细胞发生破裂而死亡，影响微生物所需基本物质的传输，破坏细胞合成酶的活性，用中断DNA复制的形式阻止微生物繁殖。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付