| 牌号简介 About |
|---|
| LL6800N树脂是一种线性低密度聚乙烯，辛烯-1共聚物，溶液法生产，用于吹塑薄膜挤出，具有优良的机械性能。它含有抗阻塞剂、加工助剂和抗氧化剂添加剂。 LL6800N resin is a Linear Low Density Polyethylene for blown film extrusion with excellent mechanical properties. Applications: Heavy-duty bags; liners; LDPE and HDPE blends; packages for general use. Additive: Antiblocking Processing Aid Process: LL6800N resin should be processed on specific extruders for LLDPE. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 200 to 220° and blends with LDPE with a maximum ratio of 30%. Recommended blow up ratio: 1.8 to 3:1. |
产品描述 Product Description
用途：薄膜;衬里;包装;袋子;混合;
加工条件：吹塑薄膜
性能特点： 抗结块性; 抗氧化; 辛烯共聚单体; High anti-blocking,Inoxidizability,Octene copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.921 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.75 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，100 µm，吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
MD，断裂，100 µm，吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
||
|
TD，断裂，100 µm，吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
MD，断裂，100 µm，吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
弯曲模量 Flexural Modulus |
注册或登录后
所有资料免费
|
||
|
1% 正割，TD，100 µm，吹塑薄膜 1% secant, TD, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
MPa | ASTM D790 |
|
1% 正割，MD，100 µm，吹塑薄膜 1% secant, MD, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
MPa | ASTM D790 |
|
落锤冲击 Gardner Impact |
注册或登录后
所有资料免费
|
||
|
100 µm，吹塑薄膜 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
g | ASTM D1709 |
|
撕裂强度 tear strength |
注册或登录后
所有资料免费
|
||
|
TD，100 µm，吹塑薄膜 TD, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
g | ASTM D1922 |
|
MD，100 µm，吹塑薄膜 MD, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
g | ASTM D1922 |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
注册或登录后
所有资料免费
|
||
|
60°，100 µm，吹塑薄膜 60 °, 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
ASTM D2457 | |
|
雾度 Haze |
注册或登录后
所有资料免费
|
||
|
100 µm，吹塑薄膜 100 µ m, blow molded film |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
力劲商标被认定为“中国著名商标”
2016-07-01 力劲科技集团有限公司旗下全资子公司力劲机械(深圳)有限公司，已收到国家工商总局商标局关于认定1705641号图形商标为驰名商标的批复，这标志着力劲集团所持有的“力劲LK”商标正式被认定为“中国驰名商标”。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付