Baydul- 660 IBS是一种用于反应注射成型(RIM)工艺的黑色、硬质聚氨酯结构泡沫体系。该系统包括一个专门设计的交互式吹扫系统(IBS),作为两个反应性液体成分提供。A组分是一种聚合物二苯基甲烷二异氰酸酯(PMDI),B组分是一种不含CFC-或HCFC发泡添加剂的配方多元醇体系。注意:由于可能存在颜料沉淀,在将桶中的内容物输送到日计量箱之前,应彻底搅动成分B。Baydur 660 IBS系统是为通用应用而设计的,用于工业和娱乐市场。这些应用通常利用了材料的强度、优异的表面光洁度和大零件性能。与任何产品一样,在给定应用中使用Baydur 660 IBS系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Baydur 660 IBS is a black-pigmented, rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Compo- nent B is a formulated polyol system containing no CFC- or HCFC-blowing additives. Note: Component B should be agitated thoroughly prior to delivery of contents of the drum to the day tank due to possible pigment settling. The Baydur 660 IBS system was designed for general-purpose applications and is used in industrial and recreational markets. The applications typically take advantage of the material's strength, excellent surface finish, and large part capability. As with any product, use of the Baydur 660 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.479 | g/cm³ | ASTM D792 |
收缩率 Shrinkage |
|||
MD:6.35 mm MD:6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
内部方法 | ||
-- -- 2 |
8.8 | kJ/m² | 内部方法 |
-- -- 3 |
9.0 | kJ/m² | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,6.35 mm Shaw D, 6.35 mm |
55 | ASTM D2240 | |
邵氏 D,12.70 mm Shore D, 12.70 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
弯曲模量 Flexural Modulus |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
压缩强度 compressive strength |
ASTM D695 | ||
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
12.7 mm 12.7 mm |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
ASTM D648 | ||
0.45 MPa,未退火,6.35 mm 0.45 MPa, unannealed, 6.35 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,12.7 mm 0.45 MPa, unannealed, 12.7 mm |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.5 |
3 0.25 in |
【新闻资讯】查看全部
生态文明贵阳国际论坛“陆地微塑料研讨会”
2018-07-31 近年来,全球对海洋环境和海岸微塑料污染带来的生态效应、渔业影响和健康风险日益关注。在7月初举行的生态文明贵阳国际论坛“海洋微塑料研讨会”高峰会上,世界各国再次聚焦海洋微塑料问题。这也是该论坛举办十年来首次将“微塑料防治”作为主题,呼吁人们关注微塑料污染,保护海洋生态环境。 塑料垃圾是海洋不能承受之重。据统计,全球每年约有1000万―2000万吨的塑料垃圾进入海洋,随时间的流逝破碎成不计其数的塑料微粒进入水体中,能够存在数百年时间。作为环境中的一类新型污染物,微塑料将对海洋生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |