Starex LX-0987EXS是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 Starex LX-0987EXS is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Appliances. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
1.05 | g/cm³ | ISO 1183 |
|
1.05 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
220℃,10.0kg 220℃,10.0kg |
12 | g/10min | ASTM D1238 |
220℃,10.0kg 220℃,10.0kg |
13 | g/10min | ISO 1133 |
收缩率 Shrinkage |
ISO 2577 | ||
TD:3.2 mm TD:3.2 mm |
0.60 to 0.70 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ISO 2577 | |
MD:3.2 mm MD:3.2 mm |
% | ISO 2577 | |
吸水率 Water Absorption |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ASTM D256 | ||
23℃ 23℃ 5 |
kJ/m² | ISO 180-1A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ISO 75-2/A | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/A | |
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ISO 75-2/B | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,4.0 mm 0.45 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temperature |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Flexural Modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Flexural Modulus 4 |
MPa | ISO 178 | |
弯曲强度 Flexural Strength 3 |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength 4 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.11 in/min |
4 0.079 in/min |
5 Thickness: 4mm |
【新闻资讯】查看全部
浙江石化业前三季业绩超预期
2017-11-30 近日,中国化工报记者从浙江省石化行业三季度经济运行座谈会上获悉,今年以来,全省石化工业运行态势持续向好,主要指标平稳较快增长,总体情况明显好于预期。与会代表认为,今年环保风暴席卷全国,大量化工企业被停限产,但浙江石化行业得益于近年来持续开展的环保整治和产业转型提升工作,先行动、先受益,已经确立了先发优势。 浙江省统计局数据显示:前三季度,全省规模以上石化工业实现总产值8381.6亿元,同比增幅17.4%,高出全省平均水平3.5个百分点;实现主营业务收入8253.7亿元,同比 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |