| 牌号简介 About |
|---|
| SABIC PP化合物7705 SABIC® PPcompound 7705是一种填充矿物的改性聚丙烯。这种材料结合了高耐刮性、高刚度、良好的冲击性和高流动性。这种材料具有很宽的加工窗口和良好的物理性能。典型应用包括美观的汽车内部零件，如仪表板、上下仪表板、门板和装饰件。SABIC® PPcompound 7705是指定的汽车级。SABIC PP化合物7705 SABIC PP化合物7705是一种矿物填充、冲击改性的聚丙烯TPO。这种材料结合了抗冲击，耐刮擦，热稳定性和汽车内部紫外线稳定性。IMDS是16161010。 SABIC® PPcompound 7705 is a mineral filled modified polypropylene. This material combines high scratch resistance, high stiffness, good impact and high flow. This material has a very broad processing window combined with good esthical performance. Typical applications include esthetical automotive interior parts such as instrument panels, lower and upper dashboard, door panels and trim. SABIC® PPcompound 7705 is a designated automotive grade. |
产品描述 Product Description
用途：汽车领域的应用;汽车仪表板;汽车内部装备;汽车内部零件;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 热稳定性好; 耐刮擦; 流动性高; 冲击性能好; 耐候抗UV; Good Rigidity,Weather resistance is good,High impact resistance,High liquidity,High scratch resistance,Heat Stabilized
紫外线：UV Stabilized
填料：矿物
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.05 | g/cm³ | ASTM D792 |
|
密度 Density |
1.04 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
22 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
60 | ISO 868 | |
|
拉伸模量 Tensile modulus 2 |
1910 | MPa | ASTM D638 |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus |
|||
|
50 mm跨距 50 mm span 4 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ 6 |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ 7 |
ISO 179/1eA | ||
|
悬臂梁缺口冲击强度 Izod Notched Impact strength 6 |
ISO 180/1A | ||
|
23℃，3.2mm 23℃，3.2mm 8 |
J/m | ASTM D256 | |
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength 8 |
|||
|
23℃，3.2 mm 23℃，3.2 mm 8 |
ASTM D4812 | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 9 |
ASTM D3763 | ||
|
-30℃，Energy at Peak Load -30℃，Energy at Peak Load |
J | ASTM D3763 | |
|
0℃，Energy at Peak Load 0℃，Energy at Peak Load |
J | ASTM D3763 | |
|
23℃，Energy at Peak Load 23℃，Energy at Peak Load |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT 6 |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed 6 |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed 6 |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temperature |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
线性热膨胀系数 Coeff.of linear therm expansion |
|||
|
TD：-30~100℃ TD：-30~100℃ |
1/℃ | ISO 11359-2 | |
|
MD：-30~100℃ MD：-30~100℃ |
1/℃ | ISO 11359-2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.079 in/min |
| 5 0.051 in/min |
| 6 方法 I (三点负荷) |
| 7 80*10*4mm, Cut |
| 8 80*10*4 mm, Cut |
| 9 63.5*12.7*3.2mm, Cut |
| 10 21.7 ft/sec |
|
【新闻资讯】查看全部 
未来三年我国大力推进重点领域5G应用
2021-07-22 搜料网资讯： 5G建设提速的同时，应用的广度和深度正在拓展。记者日前从工信部了解到，在工信部、中央网信办、国家发改委等十部门印发的《5G应用扬帆行动计划（2021-2023年）》中， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付