| 牌号简介 About |
|---|
| 材料类型：黑色氟橡胶化合物，硬度邵尔A 65~75。基于含氟量很高的过氧化物固化氟弹性体，具有优异的耐化学品性能。特点：后固化时间短，铸模流动性好，脱模性好，对硅橡胶（VMQ）的粘合性能改善较少，具有优异的耐化学性：酒精燃料，蒸汽酸，含有胺的化学品。工艺方法：适用于压缩、转移、注射和挤出成型工艺。用途：FKM-VMQ型涡轮增压软管内层。实验室测试固化条件：压力固化：10分钟@170°C。烘箱：（1+4）小时@230°C Material Type: Black color fluoroelastomer compound, hardness Shore A 65~75. Based on peroxide curable fluoroelastomer with very high fluorine content which brings outstanding chemicals resistance properties. Features: Short post cure time Excellent mold flow and mold release, resulting in less flash Improved bonding property to silicone rubber (VMQ) Extraordinary chemical resistance: Alcohol Fuel Steam Acids Chemicals containing amines. Process Methods: Suitable for compression, transfer, injection and extrusion molding processes. Applications: The inner layer of FKM-VMQ type turbo hoses. Lab Testing Curing Condition: Press Curing: 10min@170°C. Oven: (1+4)hrs@230°C |
产品描述 Product Description
用途：管道;
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 耐酒精; 含脱模剂; 耐酸; 耐化学性; 低飞边毛刺; 耐蒸汽; 耐燃油; 易流动; 可粘结性; 易加工; Excellent Processability,Ethanol tolerance,Good liquidity,Good stripping performance,Acidproof,Solvent resistance,Resistance to the steam,Agglomerability,Low flash,Fuel resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.98 | g/cm³ | ASTM D792 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
73 | ASTM D2240 | |
|
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
24.3 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
220 | % | ASTM D412 |
|
压缩形变 Compression deformation 2 |
|||
|
200℃，70 hr 200℃，70 hr 2 |
22 | % | ASTM D395 |
|
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
空气中拉伸强度的变化率 Change in Tensile Strength in Air |
|||
|
250℃，70 hr 250℃，70 hr |
% | ASTM D573 | |
|
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air |
|||
|
250℃，70 hr 250℃，70 hr |
% | ASTM D573 | |
|
空气中硬度计硬度的变化率 Change in Durometer Hardness in Air |
|||
|
250℃，70 hr 250℃，70 hr |
ASTM D573 | ||
|
拉伸强度的变化率 Change in Tensile Strength |
|||
|
23℃，70 hr，C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
|
极限伸长率的变化率 Change in Ultimate Elongation |
|||
|
23℃，70 hr，C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
|
邵氏硬度的变化率 Change rate of Shore hardness |
|||
|
23℃，70 hr，在基准燃料C中 23 ℃, 70 hr, in reference fuel C |
ASTM D471 | ||
|
体积变化 Volume change |
|||
|
23℃，70 hr，C级标准燃料 23 ℃, 70 hr, C-grade standard fuel |
% | ASTM D471 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 6 mm Buttons |
|
【新闻资讯】查看全部 
化工巨头齐涨价！10月涨价合集
2022-10-11 扫描上图二维码，可以免费下载 搜料 APP 东洋苯乙烯株式会社宣布，将从10月1日起提高聚苯乙烯（PS）树脂和阻燃聚苯乙烯（PS）树脂的价格，其中GP等级、HI等级、特殊等级、阻燃等级 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付