牌号简介 About |
---|
g-lex是一种聚碳酸酯化合物,在过去的15年里,它是由特定的和认可的原料制成的。它以其在各种温度下的高抗冲击性而闻名。它具有优异的耐热性,所有等级均通过850oC电热丝测试,测试温度为1.0毫米。高流动等级特别适用于薄壁、长流动长度的应用。G-LEX符合所有回收指令,可正常回收。在第一次使用后,树脂可以以类似的方式重新研磨和再利用,或者在要求较低的应用中级联再利用。典型的应用包括电气产品、照明、电信、电器和安全装置以及其他强度和影响很重要的应用。这种材料有黑色、自然色和最半透明、半透明和不透明的颜色。 G-Lex is a polycarbonate compound that has been made from a specified and approved feedstock for the last fifteen years. It is noted for its high impact resistance over a wide range of temperatures. It has excellent heat resistance and all grades pass the 850oC glow wire test at 1.0mm. The high flow grade is particularly suited to thin wall, long flow length application. G-Lex complies with all recycling directives and can be recycled in the normal way. After its first application the resin can be reground and reused either in a similar manner or cascaded down for reuse in less demanding applications. Typical applications include electrical goods, lighting, telecommunications, appliances and security devices and other applications where strength and impact are important. This material is available in Black and natural and most semi translucent, translucent and opaque colours. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
12 | g/10min | ISO 1133 |
收缩率 Shrinkage 1 |
0.50 到 0.70 | % | ISO 2577 |
吸水率 Water Absorption |
|||
平衡,23℃,85% RH 平衡,23℃,85%RH |
0.35 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2300 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
ISO 527-2/50 | ||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temperature |
|||
B120 B120 |
℃ | ISO 306/B120 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 500 bar |
【新闻资讯】查看全部 ![]()
又一日企突然关门,1500员工临失业,日本推进“去中国化”?
2020-12-05 搜料网资讯: 前段时间,史丹利百得关闭了深圳工厂,引发了不少热议。如今,又一家外资工厂突然关闭,让人措手不及,上千人面临失业,它就是升龙科技。 公开资料显示,升龙科技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |