ADVANCENE™ EM-4925-AAH高密度聚乙烯树脂专门设计用于间歇或连续吹塑设备中,以生产尺寸高达30升的容器,这些应用要求结合卓越的环境应力抗裂性(ESCR)和高冲击强度。ADVANCENE™ EM-4925-AAH高密度聚乙烯树脂也被认为是一种多用途吹塑树脂,设计用于高速生产吹塑容器,用于包装家用工业化学品(例如洗涤剂、漂白剂、织物柔软剂)、洗漱用品和化妆品(例如洗发水、面霜、洗剂等)健康和医疗辅助设备。此外,它可以吹塑成其他薄壁零件和家居用品,也可以挤压成型材或片材。主要特点是具有优异的抗环境应力开裂性能。冲击强度高。良好的挤压特性。 ADVANCENE™ EM-4925-AAH HDPE Resin is specifically designed for use in either intermittent or continuous blow molding equipment to produce containers up to 30 liters in size - applications that require the combination of outstanding environmental stress crack resistance (ESCR) and high impact strength. ADVANCENE™ EM-4925-AAH HDPE Resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g. detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.) health and medical aids. In addition, it can be blow molded into other thin-walled parts and houseware items, and can also be extruded into profiles or sheets. Main Characteristics Outstanding environmental stress crack resistance. High impact strength. Good extrusion characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.949 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
25 | g/10min | |
抗环境应力开裂 ESCR |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 |
180 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
|||
-- -- 2 |
210 | kJ/m² | ASTM D1822 |
-- -- |
kJ/m² | ISO 8256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Brittle Temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Flexural Modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790-B |
备注 |
---|
2、Type S |
【新闻资讯】查看全部 ![]()
印度石油巨头将大幅扩大石油勘探
2022-01-08 搜料网资讯: 据世界能源2021年12月31日消息:印度石油部长周四表示,印度国有石油天然气公司(ONGC)计划到2025年将其勘探和生产面积扩大四倍。作为世界第三大石油进口国,印度寻求减 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |