牌号简介 About |
---|
特点和优点组成:偏氟乙烯和六氟丙烯的二元聚合物中粘度工艺目标:注射、传递成型和压延与低氟聚合物相比提高了耐化学性与优良的压缩永久变形性与低氟聚合物的性能瑞公司固化技术 Features and Benefits Composition: di-polymer of vinylidene fluoride and hexafluoropropylene Medium viscosity Process targets: injection and transfer molding and calendering Improved chemical resistance compared to lower percent fluorine fluoropolymers Excellent compression set resistance compared to lower percent fluorine fluoropolymers Proprietary incorporated cure technology |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.85 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
37 | MU | |
氟含量 Fluorine content |
69 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
77 | ASTM D2240 | |
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
15.2 | MPa | |
100% 应变 100% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
MH(177℃) MH(177℃) |
J | ||
ML(177℃) ML(177℃) |
J | ||
t'50(177℃) t'50(177℃) |
min | ||
t'90(177℃) t'90(177℃) |
min | ||
ts2(177℃) ts2(177℃) |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tr10 Tr10 |
℃ | ASTM D1329 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
科思创中国区总裁:聚氨酯市场趋向明年会持续
2017-12-11 “未来不管TDI还是MDI,总体趋势向好,(它们的)增长应该会高于GDP的增长,这个趋势未来还会继续。”刚刚履新的科思创中国区总裁盛秉勇(Bjoern Skogum)近日在接受采访时对聚氨酯行业和TDI、MDI两大品种的趋势做出自己的研判。 他告诉记者,聚氨酯是一个非常有意思的材料。以TDI来说,其市场主要靠供求驱动,有些工厂出了问题,不能满负荷开工生产,就会造成供应紧张。因此,TDI的价格主要就由市场上产品的供应来决定。而MDI过去几年有一点产能过剩的问题,目前来看比以前 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |