公司信息及水印






牌号简介 About |
---|
Durethan®AKV 35 h2 SR1 901510(干燥)PA 66, 35%玻璃纤维、注塑、热老化稳定,提高表面光洁度。 Durethan® AKV35H2.0 901510 SR1 (Dry) PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV35H2.0 901510 SR1 PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV35H2.0 901510 SR1 PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, improved surface finish |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.41 | g/cm³ | ISO 1183 |
收缩率 Shrinkage |
|||
TD:300℃,2.0 mm TD:300℃,2.0 mm |
1.0 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs |
0.090 | % | ISO 294-4 |
MD:300℃,2.0 mm MD:300℃,2.0 mm |
0.32 | % | ISO 294-4 |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs |
0.070 | % | ISO 294-4 |
TD:300℃,3.0 mm TD:300℃,3.0 mm |
% | ISO 2577 | |
TD:120℃,3.0 mm,2 hrs TD:120℃,3.0 mm,2 hrs |
% | ISO 294-4 | |
MD:300℃,3.0 mm MD:300℃,3.0 mm |
% | ISO 2577 | |
MD:120℃,3.0 mm,2 hrs MD:120℃,3.0 mm,2 hrs |
% | ISO 2577 | |
吸水率 Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178-A | |
弯曲强度 Flexural Strength |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Flexural Strain |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temperature |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 80°C MT, 600 bar |
3 60x60x2; MT 80°C; 600 Bar |
4 60x60x2 |
5 60x60x2mm |
6 150x105x3mm, 80°C MT, 400 bar |
7 150x150x3; MT 80°C; 400 Bar |
8 150x150x3 |
9 150x105x3mm |
10 0.079 in/min |
11 2 mm/min |
12 Pull Rate: 2 mm/min; 50% RH |
13 10°C/min |
14 程序 A |
【新闻资讯】查看全部 ![]()
强强联手!盛虹石化与中石化十公司签署战略合作协议
2022-02-13 2月9日,盛虹石化产业集团与 中石化 第十建设有限公司(简称中石化十公司)战略合作签约仪式在连云港隆重举行。中石化十公司执行董事、党委书记吴忠宪、盛虹控股集团董事长缪汉 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |