牌号简介 About |
---|
Lexan 4504树脂高耐热聚碳酸酯共聚物,在264 psi下提供290F的DTUL。FDA食品接触有限颜色。自2008年1月15日起,该等级将不再支持生物相容性信息,不应用于需要生物相容性的医疗应用。替代等级HPH4504。 High heat resistant polycarbonate copolymer, provides DTUL of 290F at 264 psi. FDA food contact compliant in limited colors. Effective January 15th, 2008 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HPH4504. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
特定体积 Specific volume |
0.830 | cm³/g | ASTM D792 |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
3.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
3.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
24hr 24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ASTM D256 | ||
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
落锤冲击 Gardner Impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
拉伸冲击强度 Tensile impact strength 9 |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 11 | |
维卡软化温度 Vicat Softening Temperature |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
-40 到 95℃ -40 to 95 ℃ |
cm/cm/℃ | ASTM E831 | |
比热 specific heat |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal Conductivity |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
|||
电气性能 ELECTRICAL |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
相比漏电起痕指数 Comparative Tracking Index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High Voltage Arc Track Rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
1.50 mm 1.50 mm |
UL 94 | ||
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Light Transmission |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 Flexural Strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 Type S |
10 80*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部 ![]() |
科莱恩2017中国销售额增长13%,中国战略步入正轨 特殊化工品生产商科莱恩今天公布,企业在执行中国发展战略层面获得了优良进度。
坐落于中国上海市的科莱恩一体化产业园区 2017年销量提升13% 在2017年公布这一发展战略以后,科莱恩不断贯彻自主创新和可持续发展观核心理念,改进整治、提升生产能力并提升当地协作。根据这种措施,科莱恩坚信可以在二零二一年在中国完成销售总额翻一番的总体目标,将销售总额提升至10多亿元瑞士法郎。 科莱恩实行联合会组员顾培楠(Christian Kohlpaintner)在中国杭州市举行的科莱恩第八届“界定将来”交流会上表明:“对科莱恩中国区来讲,17年是取得成功的一年,销售总额提升了13%,盈利率也获得了提高。大家相信,根据执行总体的提高方案,并不断融入中国的销售市场和商业服务思维方式,到二零二一年,我们可以在二零一五年的销售总额基本上翻一番。” 中国针对科莱恩完成全方位提高发展战略尤为重要。因此,企业已在各行各业付诸行动,以求改善在这里一关键的销售市场的影响力。中国产业链已经寻找可以产生高些使用价值的技术性驱动器型解决方法,并将可以适配自然环境的化工厂解决方法放置优先选择影响力,伴随着中国产业链的持续升級,科莱恩早已占有了把握住这种提高机遇的有益部位。 在中国增加两个生产制造设备 17年,科莱恩防腐剂业务流程模块在中国增加了两个生产制造设备,根据例如此类的生产能力扩大,能够使企业考虑日益突出的当地要求,拉进与顾客和原材料经销商的间距。 创建新中外合资企业 除此之外,根据创建新的中外合资企业、建立合作方关联及其与中国当地公司和研究室创建其他方式的协作,这类间距被进一步拉进。 在过去的一年里,科莱恩与北京市天罡改性剂有限责任公司公司建立了一家中外合资企业,致力于回应日益突出对中国当地生产制造的光稳定剂的要求。 除此之外,科莱恩还与中国较大的石油化工设备公司中国石油化工签定了一份关键的合作合同。根据与上海交大签定合作备忘录(MOU),科莱恩持续了与中国学界进行当地合作自主创新的趋势。 发展电商市场销售 另外,科莱恩也希望根据在阿里巴巴网集团公司主打产品的B2B商业服务服务平台1688.com开设官方旗舰店(https://clariant.1688.com/),在大中华地区扩张电商市场销售。 创建以中国高层住宅技术人员核心损益表的整治方式 最终,根据创建一个由中国高层住宅技术人员承担损益表的全新升级区域治理方式,大大的改进了发展战略开设和融洽。上海市区创建的科莱恩一体化产业园区(OCC)方案于今年完工,它包含一个综合型的地区总公司和自主创新设备。到时候,所述这种好处将在科莱恩一体化产业园区获得进一步的呈现。 来源于:CPRJ 中国塑胶硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。