公司信息及水印






牌号简介 About |
---|
TENITE纤维素塑料以其优良的性能平衡而闻名——韧性、硬度、强度、表面光泽、透明度和温暖感。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低,表面越硬,耐热性越高,刚性越高,拉伸强度越高,尺寸稳定性越好。增塑剂含量越高,冲击强度越高。Tenite纤维素塑料有天然、透明、精选的琥珀色或烟雾透明和黑色半透明。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素285-20的增塑剂含量为20%,含有防臭面具。 Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulose plastics are available in natural, clear, selected ambers, or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-20 has a plasticizer level of 20% and contains an odor mask. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
吸水率 Water Absorption |
|||
23℃,24hr 23℃,24hr |
1.2 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ASTM D256 | ||
-40℃ -40℃ |
注册或登录后
所有资料免费
|
J/m | ASTM D256 |
23℃ 23℃ |
注册或登录后
所有资料免费
|
J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT 2 |
注册或登录后
所有资料免费
|
||
1.8 MPa,退火 1.8 MPa, annealed 2 |
注册或登录后
所有资料免费
|
℃ | ASTM D648 |
0.45 MPa,退火 0.45 MPa, annealed 2 |
注册或登录后
所有资料免费
|
℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temperature 2 |
注册或登录后
所有资料免费
|
℃ | ASTM D1525 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可溶性物质损失 Loss of soluble substances |
注册或登录后
所有资料免费
|
||
23℃ 23℃ |
注册或登录后
所有资料免费
|
% | ASTM D570 |
加热减量 Heating reduction |
注册或登录后
所有资料免费
|
||
72 hrs,80℃ 72 hrs,80℃ |
注册或登录后
所有资料免费
|
% | ASTM D707 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
||
断裂,23℃ Fracture, 23 ℃ |
注册或登录后
所有资料免费
|
MPa | ASTM D638 |
屈服,23℃ Yield, 23 ℃ |
注册或登录后
所有资料免费
|
MPa | ASTM D638 |
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
||
断裂,23℃ Fracture, 23 ℃ |
注册或登录后
所有资料免费
|
% | ASTM D638 |
弯曲模量 Flexural Modulus |
注册或登录后
所有资料免费
|
||
23℃ 23℃ |
注册或登录后
所有资料免费
|
MPa | ASTM D790 |
弯曲强度 Flexural Strength |
注册或登录后
所有资料免费
|
||
屈服,23℃ Yield, 23 ℃ |
注册或登录后
所有资料免费
|
MPa | ASTM D790 |
洛氏硬度 Rockwell hardness |
注册或登录后
所有资料免费
|
||
R 级 R-level |
注册或登录后
所有资料免费
|
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Conditioned 4 hours at 70°C (158°F) |
【新闻资讯】查看全部 ![]()
凯赛携手西门子打造生物制造智能工厂
2017-06-06 西门子与凯赛生物产业有限公司今天在北京签署合同,双方将携手帮助凯赛新疆乌苏项目建设先进的智能工厂。在双方的合作中,西门子提供的数字化企业解决方案横跨了农产品加工、生物制药、化工材料和纺丝四个行业的典型工艺段。该工厂由凯赛投资建设,以生物新型材料制造为主,工厂一期预计实现年产5万吨戊二胺、3万吨长链二元酸、10万吨生物基聚酰胺和3万吨短纤。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Tenite™ Butyrate 285A2R30020 Natural, Trsp证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)