牌号简介 About |
---|
是一种丙烯酸封端共挤出的ABS片材,可制成两层或三层复合材料。亚克力帽子赋予一个非常高的光泽,充满活力的色彩,具有卓越的图像深度,出色的紫外线防护,耐化学性,韧性和良好的成型性。应用:Prime ABS Weather-X 200的性能特点使其成为应用的首选材料,包括船舶、个人船艇、休闲车、草坪/花园、建筑/建筑和汽车配件。加工:表面温度=325-360°F模具温度=150-175°F模具温度@170°F模具收缩率为.004-.008英寸/英寸。与丙烯酸相比,ABS可以吸收更多的辐射能;因此,表面温度可能增加得更快。应注意将表面温度保持在325°F-360°F,以避免丙烯酸盖起泡、燃烧和颜色/光泽变化。表面处理:Prime ABS Weather-X 200可使用机械方法(如螺栓、螺钉或夹具)或化学方法(如胶结)进行连接。用丙烯酸改性钻头钻共挤板时,一定要从丙烯酸侧退出,但用标准钻头钻时,一定要从基底侧退出。为了准确和安全,钻孔时应夹紧Prime ABS Weather-X 200。请与Primex塑料公司代表联系,了解有关表面处理、制造或热成型工艺的更多信息。颜色、纹理和功能:Prime ABS Weather-X 200颜色可匹配,以满足您的特定要求。表面通常是高光泽,但纹理,如小腿纹理,H/C,F/L H/C,莱凡特1和塞维利亚。 Is an acrylic capped co-extruded ABS sheet, which can be produced as a two or three multilayer composite. The acrylic cap imparts a very high gloss, vibrant colors with superior depth of image, excellent UV protection, chemical resistance, toughness and excellent formability. Applications: The performance features of Prime ABS Weather-X 200 make it the material of choice for applications, including marine, personal watercraft, recreational vehicles, lawn/garden, building/construction and automotive accessories. Processing: Surface Temp = 325-360°F Mold Temp = 150-175°F De-mold @ 170°F Mold shrink is .004-.008 in/in. ABS may absorb greater amounts of radiant energy than acrylic; thus, surface temperatures may increase more rapidly. Care should be taken to maintain the surface temperature at 325°F-360°F to avoid blistering, burning and color/gloss shift of the acrylic cap. Finishing: Prime ABS Weather-X 200 can be joined using mechanical methods such as bolts, screws or clamps, or chemical methods such as cementing. When drilling coextruded sheet with an acrylic modified drill bit, be sure to exit from the acrylic side but when drilling with a standard bit, be sure to have the bit exit from the substrate side. For accuracy and safety, Prime ABS Weather-X 200 should be clamped during drilling. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime ABS Weather-X 200 can be color matched to meet your specific requirements. The surface is typically high gloss but textures such as calf grain, H/C, F/L H/C, Levant 1 and Seville are available. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
8.9 | g/10min | ASTM D1238 |
收缩率 Shrinkage |
|||
MD MD |
0.30 到 0.50 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
36.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
22 | % | ASTM D638 |
弯曲模量 Flexural Modulus |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
ASTM D256 | ||
0℃,3.2mm 0℃,3.2mm |
J/m | ASTM D256 | |
22℃,3.2mm 22℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D523 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
De(mold Temperature) De(mold Temperature) |
℃ | ||
模具温度 Mold temperature |
|||
other other |
℃ | ||
Surface Temperature Surface Temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
智能模具代表我国模具技术的展开新方向
2016-06-17 我国模具工业近年来发展很快,据不完全统计,2004年我国模具生产厂点约有3万多家,从业人员80万人,2014年模具行业的发展保持良好势头,模具企业总体上订单充足,任务饱满,模具企业和厂商约有8万家,从业人员达到200万人,全国模具总产值由610亿元增长到1.8万亿元。 同时,这也说明中国的模具生产技术有了很大的提高,模具生产水平有些已接近或达到国际水平。2005年模具进口达20.68亿美元,比上一年增长14.07%,这说明高技术含量模具仍远远满足不了国内市场需要。2013年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |