Fortus 3D生产系统Ultem 9085的生产级热塑性塑料是一种用于直接数字制造和快速成型的阻燃高性能热塑性塑料。由于其高强度重量比和FST(火焰、烟雾和毒性)等级,因此非常适合运输行业。这种独特的材料的现有认证使其成为商业运输行业的一个极好的选择-特别是航空航天,海洋和地面车辆。与Fortus 3D生产系统相结合,Ultem 9085允许设计和制造工程师生产完全功能性的零件,这些零件非常适合高级功能原型或最终用途,而无需传统工具的成本或交付周期。 Production-Grade Thermoplastic for Fortus 3D Production Systems ULTEM 9085 is a flame retardant high performance thermoplastic for direct digital manufacturing and rapid prototyping. It is ideal for the transportation industry due to its high strength-to-weight ratio and its FST (flame, smoke, and toxicity) rating. This unique material's preexisting certifications make it an excellent choice for the commercial transportation industry - especially aerospace, marine and ground vehicles. Combined with a Fortus® 3D Production System, ULTEM 9085 allows design and manufacturing engineers to produce fully functional parts that are ideal for advanced functional prototypes or end use without the cost or lead time of traditional tooling. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ASTM D792 |
Thickness(Layer Capability) Thickness(Layer Capability) |
254.0 到 330.2 | µm | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
|||
3.18 mm 3.18 mm 3 |
2220 | MPa | ASTM D638 |
拉伸强度 tensile strength 3 |
|||
3.18 mm 3.18 mm 3 |
71.7 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
断裂,3.18 mm Fracture, 3.18 mm 3 |
6.0 | % | ASTM D638 |
弯曲模量 Flexural Modulus 4 |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength 4 |
MPa | ASTM D790 | |
压缩模量 Compressive Modulus |
MPa | ASTM D732 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
|||
6.35 mm 6.35 mm |
MPa | ASTM D732 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D256-A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD MD |
1/℃ | ASTM E228 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 5 , 6 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 6 |
ASTM D150 | ||
耗散因数 Dissipation factor 6 |
ASTM D150 | ||
体积电阻 Volume Resistivity 6 |
ohms | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
FAA FAA |
FAR 25.853 | ||
NBS烟雾密度 NBS Smoke Density |
ASTM F814/E662 | ||
flaming flaming |
ASTM F814/E662 | ||
non-flaming non-flaming |
ASTM F814/E662 | ||
OSU总放热量 OSU total heat release |
FAR 25.853 | ||
2 min test 2 min test |
kW·min/m² | FAR 25.853 | |
5 min test 5 min test |
kW/m² | FAR 25.853 | |
垂直燃烧-60秒 Vertical combustion -60 seconds |
|||
1.02 到 6.35 mm 1.02 to 6.35 mm |
sec | FAR 25.853 | |
放热 exothermic |
|||
65/65,<40HR Peak,1.52 mm 65/65,<40HR Peak,1.52 mm |
FAR 25.853 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Outgassing Outgassing |
ASTM E595 | ||
Collected Volatile Condensable Material(CVCM) Collected Volatile Condensable Material(CVCM) |
% | ASTM E595 | |
Total Mass Lost(TML) Total Mass Lost(TML) |
% | ASTM E595 | |
Water Vapor Recovered(WVR) Water Vapor Recovered(WVR) |
% | ASTM E595 | |
抗真菌性 Antifungal activity |
|||
Method 508.6 Method 508.6 |
MIL STD-810G |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 0.20 in/min |
3 方法 I (三点负荷), 0.050 in/min |
4 方法A(短时间) |
5 All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
【新闻资讯】查看全部 ![]()
朗盛2021财年开局充满信心 进军电池化学品领域
2021-04-24 搜料网资讯: 2021年4月2日,德国特殊化学品公司 朗盛 在上海举行了年度新闻发布会,介绍其大中华区2020年财务业绩及2021年业务布局。2020年朗盛集团的销售额为61.04亿欧元,常规业务范 |
朗盛2021财年开局充满信心 进军电池化学品领域 搜料网资讯:2021年4月2日,德国特殊化学品公司朗盛在上海举行了年度新闻发布会,介绍其大中华区2020年财务业绩及2021年业务布局。2020年朗盛集团的销售额为61.04亿欧元,常规业务范围内息税折旧及摊销前利润达到8.62亿欧元,处于预计范围的上限。对于2021财年,朗盛满怀信心,并预计众多客户行业将迎来复苏。公司预估其常规业务范围内息税折旧及摊销前利润将在9亿欧元至10亿欧元之间。
朗盛亚太区总裁钱明诚表示:“中国是朗盛稳健发展的重要市场,也是疫情期间亚太地区唯一需求旺盛的市场。朗盛大中华区2020年销售额占全球总销售额的14%,保持了上一年的高水平。汽车行业显著增加的需求以及新组建的消费者保护业务板块大大促进了我们的业绩发展。” 发布会上,朗盛还宣布与全球领先的锂离子电池材料制造商广州天赐高新材料股份有限公司(下称“天赐材料”)开展合作,进军电池化学品领域。从明年开始,朗盛将在天赐材料的授权下生产锂离子电池的电解液。 钱明诚指出:“电动汽车的上升势头正在加速。目前欧洲正在兴建许多电池生产工厂。这个快速增长的市场也为朗盛提供了巨大的机遇,特别是在电池化学品领域。我们已生产了许多制造电池所需的原材料,与天赐材料的合作将使我们在这个市场中进一步站稳脚跟。” 电解液的作用是在电池中传输锂离子,因此它是锂离子电池的关键材料。通过朗盛在勒沃库森生产高性能电解液,天赐材料将成为欧洲电池厂商的本土供应商。 朗盛将在其子公司Saltigo运营的高科技工厂进行生产,Saltigo是全球领先的定制制造商。该工厂可按照最高质量要求配制电解液。Saltigo将把其丰富的化学专业知识带到合作中来,同时进一步丰富其在电解液生产领域的经验。 在发布会上,钱明诚还介绍了朗盛亚太应用开发中心(AADC)的最新进展。他表示:“该项目已于2020年12月中旬由上海化学工业区(SCIP)移交给我们,预计将于2021年中投入运营。本土创新对朗盛中国新业务的发展越来越重要,亚太应用开发中心(AADC)将面向市场,开发对高质量产品日益增长的需求。”
在市场拓展的同时,朗盛始终将可持续发展做为企业的重要战略。2019年11月,朗盛提出了到2040年将温室气体排放量从320万吨左右减少至零,实现气候中立的目标。目前这一计划进展顺利,与2019年相比,朗盛在2020年减少了14%的温室气体排放,相当于减少了41.7万吨二氧化碳。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。