| ATTANE™ NG 4701G聚乙烯树脂是一种很好的抗滥用共聚物,具有极高的抗冲击强度,结合良好的撕裂性和优异的光学性能。它还具有易于加工(低熔融温度、低挤出机安培数和低屏幕组件背压)的额外优点,由于其气泡稳定性,可以转化为优质薄膜卷。主要特点:超低密度乙烯/辛烯共聚物高性能薄膜应用符合:美国FDA 21 CFR 177.1520(c)3.2A。加拿大HPFB无异议,请参考法规了解完整细节。 ATTANE™ NG 4701G Polyethylene Resin is a great abuse resistance copolymer offering extremely high impact strength, combined with good tear and exceptional optics. It has the added benefit of being easy to process (low melt temperature, low extruder amps and low screen pack backpressure) which translates into quality film rolls due to its bubble stability. Main Characteristics: Ultra low density ethylene/octene copolymer High performance film applications Complies with: U.S. FDA 21 CFR 177.1520(c)3.2a. Canadian HPFB No Objection Consult the regulations for complete details. |
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.912 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
注册或登录后
所有资料免费
|
µm | |
|
膜刺穿强度 Membrane puncture strength |
注册或登录后
所有资料免费
|
J | 内部方法 |
|
膜刺穿力 Membrane puncture force |
注册或登录后
所有资料免费
|
N | 内部方法 |
|
膜耐刺穿性 Membrane puncture resistance |
注册或登录后
所有资料免费
|
J/cm³ | 内部方法 |
|
膜强度 Membrane strength |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
MD MD |
注册或登录后
所有资料免费
|
J/cm³ | ASTM D882 |
|
TD TD |
注册或登录后
所有资料免费
|
J/cm³ | ASTM D882 |
|
割线模量 Secant modulus |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
1% 正割,MD 1% secant, MD |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
2% 正割,MD 2% secant, MD |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
1% 正割,TD 1% secant, TD |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
2% 正割,TD 2% secant, TD |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
MD,屈服 MD, yield |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD,屈服 TD, yield |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
MD,断裂 MD, fracture |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
TD,断裂 TD, fracture |
注册或登录后
所有资料免费
|
MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
ASTM D882 | |
|
MD,断裂 MD, fracture |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
TD,断裂 TD, fracture |
注册或登录后
所有资料免费
|
% | ASTM D882 |
|
落锤冲击 Gardner Impact |
注册或登录后
所有资料免费
|
g | ASTM D1709B |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
注册或登录后
所有资料免费
|
ASTM D1922 | |
|
MD MD |
注册或登录后
所有资料免费
|
g | ASTM D1922 |
|
TD TD |
注册或登录后
所有资料免费
|
g | ASTM D1922 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
注册或登录后
所有资料免费
|
℃ | ASTM D1525 |
|
熔融温度 Melting temperature |
注册或登录后
所有资料免费
|
||
|
DSC DSC |
注册或登录后
所有资料免费
|
℃ | ISO 3146 |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
注册或登录后
所有资料免费
|
||
|
45° 45° |
注册或登录后
所有资料免费
|
ASTM D2457 | |
|
雾度 Haze |
注册或登录后
所有资料免费
|
% | ASTM D1003 |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |














支付宝
微信支付