| 牌号简介 About |
|---|
| 鲁米新MPE M 3427是以己烯为共聚单体的第二代茂金属基聚乙烯。与传统的LLDPE和第一代茂金属聚乙烯相比，鲁米新MPE M 3427的挤出压力低、缩颈低、拉伸性能好、表观控制好，产量高。这些特征与良好的光学性能相结合，带来了显著的下测量潜力。Lumicene MPE M 3427适用于消费者、食品和卫生包装领域的许多应用，如卫生膜、拉伸包装（不粘层）和层压。 Lumicene® mPE M 3427 is a second generation metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 3427 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features combined with excellent optical properties brings a significant downgauging potential. Lumicene® mPE M 3427 is suited for many applications in the field of consumer, food and hygiene packaging such as hygiene film, stretch wrap (non cling layer) and lamination. |
产品描述 Product Description
用途：薄膜;包装;食品包装;流延薄膜;层压板;拉伸缠绕;
加工条件：流延薄膜
性能特点： 抗氧化; 内缩量低; 易剥离; 己烯共聚单体; 良好的测量控制; 光学性能; Good dissection,Optical performance,Good Gauge Control,Low shrinkage,Inoxidizability,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.934 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
3.1 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
20 | µm | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，20 µm，吹塑薄膜 MD, yield, 20 µ m, blow molded film |
12.0 | MPa | ISO 527-3 |
|
TD，屈服，20 µm，吹塑薄膜 TD, yield, 20 µ m, blow molded film |
11.5 | MPa | ISO 527-3 |
|
MD，断裂，20 µm，吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，20 µm，吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，20 µm，铸造薄膜 MD, fracture, 20 µ m, cast thin film |
% | ISO 527-3 | |
|
TD，断裂，20 µm，铸造薄膜 TD, fracture, 20 µ m, cast thin film |
% | ISO 527-3 | |
|
落锤冲击 Gardner Impact |
|||
|
20 µm，铸造薄膜 20 µ m, cast thin film |
g | ISO 7765-1 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
|
MD：20 µm，铸造薄膜 MD: 20 µ m, cast thin film |
N | ISO 6383-2 | |
|
TD：20 µm，铸造薄膜 TD: 20 µ m, cast thin film |
N | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，20 µm，铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
20.0 µm，铸造薄膜 20.0 µ m, cast thin film |
% | ISO 14782 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
Toyota Racing采用聚酰胺材料3D打印赛车部件
2022-06-13 Stratasys是一家聚合物3D打印技术公司，目前是 Toyota Racing Development (TRD)的官方合作伙伴。该合作关系将在即将到来的GR Cup丰田GR86上首次亮相，3D打印生产部件是SRO America批准的新单品牌赛 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付