| 牌号简介 About |
|---|
| Amodel® A-6135 HN聚邻苯二甲酰胺（ppa）是一种35%的玻璃纤维增强树脂，具有热稳定、润滑和热水可塑性。该树脂的关键性能是在较宽的温度范围内具有较高的耐热性、高强度和刚度。它还具有低吸湿性、优异的耐化学性和优良的电气性能。Amodel® A-6135 HN树脂是理想的汽车电气和电子应用，包括连接器，插座，开关和传感器。它也是保护关键控制系统（如防抱死制动器、牵引力控制、转向、电子发动机控制、变速箱和底盘控制单元）的发动机罩下外壳的理想选择。黑色：A-6135 HN BK 324 Natural A-6135 HS NT Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, non-lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: A-6135 HN BK 324 |
产品描述 Product Description
厂家：比利时索尔维 Solvay
类别：PPA PPA
用途：电器外壳;电气/电子应用领域;机器/机械部件;连接器;动力/其它工具;金属取代;外壳;阀门/阀门部件;草坪和园林设备;汽车领域的应用;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：黑色
加工条件：水温模具注塑成型
性能特点： 低吸湿性; 热稳定性好; 机械强度好; 耐化学性; 耐高温; 易流动; 韧性好; Good Rigidity,Good flexibility,Good liquidity,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized
填料：玻璃纤维 35
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.45 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage |
ISO 294-4 | ||
|
TD TD |
0.90 | % | ASTM D955 |
|
MD MD |
0.60 | % | ASTM D955 |
|
TD TD |
1.0 | % | ISO 294-4 |
|
MD MD |
0.50 | % | ISO 294-4 |
|
吸水率 Water Absorption |
|||
|
24hr 24hr |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ISO 62 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
J/m | ASTM D256 | |
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
|||
|
1.8 MPa，退火，3.2 mm 1.8 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
熔融温度 Melting temperature |
℃ | ASTM D570 | |
|
线性热膨胀系数 Coeff.of linear therm expansion |
|||
|
TD TD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
|
MD MD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
ISO 527-2 | ||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
100℃ 100℃ |
MPa | ISO 527-2 | |
|
150℃ 150℃ |
MPa | ISO 527-2 | |
|
175℃ 175℃ |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
ISO 527-2 | ||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，24℃ Fracture, 24 ℃ |
MPa | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
|
断裂，175℃ Fracture, 175 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
ISO 527-2 | ||
|
断裂 fracture |
% | ASTM D638 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
断裂，24℃ Fracture, 24 ℃ |
% | ISO 527-2 | |
|
断裂，150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
|
断裂，175℃ Fracture, 175 ℃ |
% | ISO 527-2 | |
|
弯曲模量 Flexural Modulus |
MPa | ASTM D790 | |
|
弯曲模量 Flexural Modulus |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
100℃ 100℃ |
MPa | ISO 178 | |
|
150℃ 150℃ |
MPa | ISO 178 | |
|
175℃ 175℃ |
MPa | ISO 178 | |
|
弯曲强度 Flexural Strength |
MPa | ASTM D790 | |
|
弯曲强度 Flexural Strength |
ISO 178 | ||
|
3.50% 应变，23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
|
3.50% 应变，100℃ 3.50% strain, 100 ℃ |
MPa | ISO 178 | |
|
3.50% 应变，150℃ 3.50% strain, 150 ℃ |
MPa | ISO 178 | |
|
3.50% 应变，175℃ 3.50% strain, 175 ℃ |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
泊松比 Poisson's ratio |
ASTM E132 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
芜湖生物基材料联合创新中心成立，普立思项目即将量产！
2022-07-07 7月5日上午，由普立思生物科技股份有限公司、芜湖市人民政府和中国科学院长春应用化学研究所共同创建的芜湖生物基材料联合创新中心揭牌仪式在安徽芜湖成功举行。 中国科学院长 |
|
芜湖生物基材料联合创新中心成立，普立思项目即将量产！
7月5日上午，由普立思生物科技股份有限公司、芜湖市人民政府和中国科学院长春应用化学研究所共同创建的“芜湖生物基材料联合创新中心”揭牌仪式在安徽芜湖成功举行。
中国科学院长春应用化学研究所院士陈学思、市委书记单向前、宁波市市长、安徽工程大学校长王绍武以及市领导和普立思领导出席了揭牌仪式。
该中心的正式启动是迈向普立思和芜湖聚乳酸行业全球技术领先者目标的一小步，也是胜利的一步！
该中心的正式启动对聚乳酸的建设和发展具有重要意义。它不仅可以帮助聚乳酸实现其成为全球聚乳酸行业领导者的伟大梦想，支持聚乳酸完成全球化的伟大事业，让民族品牌和自己的技术在国际上大放异彩，也意味着聚乳酸的聚乳酸项目即将批量生产！
该中心的正式启动，是芜湖生物材料产业繁荣健康发展的里程碑。全面聚焦生物材料产业共性技术问题、前沿技术、绿色制造和产品应用的技术研究、开发和产业化；同时，该中心还将成为科技创新的开放平台。将与国内高校和知名大学开展高水平的政治、产业、学术和研究合作，力争在5至10年内建成国家生物基新材料产业创新技术高地。
作为芜湖生物材料联合创新中心的中流砥柱，普立思不会忘记初衷，牢记使命，充分发挥自身优势，积极融入产业创新生态圈，不断取得新的创新成果，并带领中心成长为中国顶尖的聚乳酸材料技术创新中心和世界领先的聚乳酸材料创新中心！
|
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
价格走势图
开始时间：
结束时间：
材料厂家：
【牌号齐全，内容全面】
全网共2500+项牌号+上游原料单体+原油价格，最长可追溯近20年价格行情
【精准，及时，权威！】
专业团队挖掘行情信息，第一时间发布行情
抱歉！该牌号暂无认证数据。
免责声明：参考价格是搜料网根据网络大数据拟合分析的结果，仅供参考。实际成交价取决但不限于以下因素：下单时间，付款方式，交货方式，数量，税费，色号，产地，项目信息。
抱歉！暂无数据。
抱歉！暂无数据。
当前牌号已加入对比
支付宝
微信支付