| 牌号简介 About |
|---|
| SABIC® LDPE 2200H2是一种低熔融流速的等级，含有低水平的防堵塞剂和中等水平的滑动剂（E=Erucamide）。这一等级显示出良好的下拉能力和良好的光学性能。应用SABIC LDPE 2200TC12通常用于需要高强度和高收缩力和包装强度的薄膜应用。典型的应用是层压和共挤薄膜。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。 SABIC® LDPE 2200H2 is a grade with a low melt flow rate and contains a low level of anti block and a medium level of slip agent (E=erucamide). This grade shows a good draw down ability and good optical properties. Application SABIC® LDPE 2200TC12 is typically used for thin film applications requiring high strength and thin shrink film with high shrink forces and wrapping strength. Typical applications are lamination and coextruded films. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
用途：薄膜;收缩性薄膜;层压板;吹膜;
加工条件：吹塑薄膜
性能特点： 流动性低; 机械强度好; 易剥离; 低密度; 光学性能; 低抗结块性; Good Rigidity,Low liquidity,Good dissection,Optical performance,Low density,Low anti-blocking
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.922 | g/cm³ | ISO 1183/A |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.33 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 Frictional coefficient |
|||
|
吹塑薄膜 Blown film |
0.20 | ASTM D1894 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
MD，50 µm，吹塑薄膜 MD, 50 µ m, blow molded film |
190 | MPa | |
|
TD，50 µm，吹塑薄膜 TD, 50 µ m, blow molded film |
MPa | ||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，50 µm，吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
|
TD，屈服，50 µm，吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁冲击强度 Izod Impact strength |
|||
|
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50.0 µm，吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003A | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻塞力 Blocking force |
|||
|
吹塑薄膜，50.0 µm Blow molded film, 50.0 µ m |
g | 内部方法 | |
|
Re-blocking - 吹塑薄膜（50.0 µm） Re blocking - blow molded film (50.0 µ m) |
g | 内部方法 | |
|
撕裂强度 tear strength 1 |
ISO 6383-2 | ||
|
MD，50 µm MD，50 µm |
kN/m | ||
|
TD，50 µm TD，50 µm |
kN/m | ||
|
memo_intro memo_intro |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Blown Film |
|
【新闻资讯】查看全部
布鲁克纳向印度包装行业推出智能薄膜消费线
2018-01-25 据报道，德国的布鲁克纳集团将在2018年印度塑料展展会(08号厅，8B52号展位)上为印度次大陆地区的包装行业提供持续成功的解决方案。 BOPET线：提高生产力，同时降低能源消耗 10.4 m工作幅宽的BOPET线降低特定的生产成本和能耗，从而获得更好的整体盈利能力，在保证了最小化单位产量的运行成本同时还降低能耗。BOPET薄膜优异的性能离不开布鲁克纳公司前几年提出的幅宽达10.4m的生产线概念。印度塑料展会上，布鲁克纳还将 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付