牌号简介 About |
---|
AvaSpire AV- 651 CF30 是AvaSpire AV-651的 30%的碳纤维增强牌号。该配方与30%碳纤增强PEEK相比,具有尺寸稳定性更好、注塑成型时更抗翘曲等优点。 在所有AV-651系列材料中,AV -651 CF30牌号具有最高的强度、刚度和耐疲劳性。此外,这种树脂通常保留了碳纤维增强PEEK的大多数有用的超高性能优势,包括耐化学性、耐疲劳性,长期热氧化稳定性。 AV- 651 CF30出色的平衡性能使之非常适合包括医疗保健、交通运输、电子、石油和天然气等行业在内的广泛的应用。这种树脂可以很容易地在标准设备上通过注射成型进行熔融加工。AV-651 CF30的熔融处理性能整体上非常接近30% 碳纤增强PEEK。在具有AV-651 CF30相同的性能特征,同时可挤出加工的情况下,低熔体流动性 AV-621 CF30 牌号被认为更适合挤塑产品。 AvaSpire® AV-651 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-651. This formulation offers some advantages relative to 30% carbon fiber reinforced PEEK which include better dimensional stability and warp resistance during injection molding. The AV-651 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-651-based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-651 CF30 makes this grade well suited for a broad range of applications across a number of industries including healthcare, transportation, electronics, oil and gas, and chemical processing. This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-651 CF30 is overall very similar to that of 30% CF reinforced PEEK. While the resin can also be extruded, the lower melt flow AV-621 CF30 grade is considered more suited for extrusion applications while offering the same property profile as AV-651 CF30. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
-- -- |
59 | J/m | ASTM D256 |
-- -- |
8.4 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength |
|||
-- -- |
590 | J/m | ASTM D4812 |
-- -- |
37 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT 4 |
|||
1.8 MPa,退火,3.2 mm 1.8 MPa, annealed, 3.2 mm 4 |
212 | ℃ | ASTM D648 |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal Conductivity |
W/m/K | ASTM E1530 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃,3.20 mm,注塑成型 Shore D, 23 ℃, 3.20 mm, injection molding |
ASTM D2240 | ||
洛氏硬度 Rockwell hardness |
|||
M 级,23℃,3.20 mm M-grade, 23 ℃, 3.20 mm |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/5 | |
-- -- 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Flexural Modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage 2 |
ASTM D955 | ||
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
吸水率 Water Absorption |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5" x 0.5" x 0.125" bars |
3 0.20 in/min |
4 200°C,2小时 |
【新闻资讯】查看全部 ![]()
金发科技全球规划 美国消费基地3月8日投产
2016-03-04 据悉,金发科技美国生产基地将于今年3月8日投产,届时将有州长、客户、供应商、行业协会等100多人参加投产仪式。另外, 金发在欧洲的基地今年中期也会投产。 金发科技美国生产基地 |
金发科技全球规划 美国消费基地3月8日投产 据了解,金发科技美国生产制造基地将于2020年3月8日投产,到时候将有市长、顾客、经销商、产业协会等100多的人报名参加投产典礼。此外, 金发在欧州的基地2020年中后期也会投产。 金发科技美国生产制造基地 美国金发公司注册地址在安娜堡,间距全世界轿车管理中心底特律仅一小时路程。所在位置显示信息了该企业进到美国轿车供应链管理的浓厚兴趣。 金发科技职工微信发朋友圈提早庆贺美国金发投产表明,2016年金发科技将宣布从印尼逐渐现代化,迈向着眼于全球比较发达经济大国的经济全球化。金发科技车用原材料工作总部的全球化战略具有了更牢靠的基本。 金发是中国较大 的车用改性工程塑料制造业企业,但伴随着中国车用塑料制品厂家增长速度的缓解,金发早已加速开发设计国外生产模式,2013年在印尼创建了该企业第一座国外生产制造基地,本厂也主要车用塑胶。而美国金发、欧州金发的陆续投产,则是显示信息了金发科技车用原材料市场部的全球化战略。 据统计,早在2015年2月3日,金发科技就在美国得克萨斯州宣布创立了控股子公司美国金发,名叫金发科技(美国)企业。2015年8月26日,美国得克萨斯州市长Rick Snyder(里克-斯奈德)驾临金发科技广州市总公司调查,彼此就将来业务流程协作等开展了友善沟通交流。2016年2月26日,美国国家商务部助手科长Arun Kumar会话金发科技领导干部,彼此开展了深入分析。 此外,据了解, 3月1日金发科技公布了公开增发应急预案,企业拟以5.49元/股的价钱公开增发个股不超过1.54每股公积金,募资不超过8.45亿人民币,扣减发行费后拟所有用以还款贷款银行和填补周转资金。 报导称,金发董事长助理彭忠泉表明,考虑到在美国等地建生产制造基地,是“那样更挨近销售市场,更关键的是,能吸引住大量国际化人才出示很有可能 。报导还称,做为一家民企,金发意识到,自身与国营企业忧于中央企业对比,拥有 诸多的薄弱点,在其中,优秀人才的匮缺是最重要的一块。在国外开设的基地,被寄托了为企业招贤纳才的殷切期望。 来源于:CPRJ 中国塑料硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- 油泵壳体
- 2019-04-16 0
- 30%碳纤维增强化合物Avaspire®AV-651 CF30具有更高的强度、刚度和抗疲劳性。将整个金属外壳更换为一个由Avaspire®PAEK成型的外壳,可在满足机油泵所需性能要求的同时减轻总重量。
- 阅读全文
油泵壳体

2-熔体体积流动速率( 400℃/2.16 kg),4.50 cm³/10min
抱歉!暂无数据。