FLEXAREN® 09002-优质乙烯-乙酸乙烯酯共聚物,含9%的乙酸乙烯酯。采用高压管工艺FLEXAREN® 09002制造,比低密度聚乙烯更具弹性,可与多种聚合物相容。它可以用相同的设备进行加工。 FLEXAREN® 09002 - high quality ethylene vinyl acetate copolymer with 9% content of vinyl acetate. Manufactured by high pressure tubular process FLEXAREN® 09002 is more elastic than LDPE and compatible with a wide range of polymers. It can be processed with the same equipment. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
0.926 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.5 | g/10min | ISO 1133 |
醋酸乙烯含量 Vinyl acetate content |
9.0 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,50 µm MD,50 µm |
28.0 | MPa | ISO 527-3 |
TD,50 µm TD,50 µm |
24.0 | MPa | ISO 527-3 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306/A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/1BA | ||
断裂 fracture |
MPa | ISO 527-2/1BA | |
50% 应变 50% strain |
MPa | ISO 527-2/1BA | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1BA |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国工程塑料机械产业明显提升
2015-11-25 随着塑料工业的快速发展,市场对塑料成型加工机设备的需求大幅度提高。许多企业通过与国外同类企业进行合资、合作和购买生产制造许可证等方式,从国外引进先进技术和设计并进行消化吸收,使我国塑料机械产业有了一个显著的提升,产品开始初步满足工程塑料加工工业的一般需求。 全球对塑料加工机械的需求预计将每年增长6.9%,达到371亿年的2017美元,这种增长或因于更好的销售,造成加速固定资产投资支出和经济增长在塑料制品的生产。 由于全球整体经济形势向好,收入提高,工程塑料产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |