| 牌号简介 About |
|---|
| AMPLIFY™ TY 1353功能性聚合物是马来酸酐接枝（MAH）聚合物。在软包装的连接层中，AMPLIFY™ TY 1353功能性聚合物可促进聚乙烯与阻隔性聚合物（如聚酰胺和乙烯-乙烯醇（EVOH））和其他极性基质的粘合。主要特点：对聚酰胺和EVOH具有优异的粘附性，优异的物理性能，吹塑和浇铸薄膜的各种工艺和使用温度均符合：美国FDA 21 CFR 175.105 EU，编号10/2011有关完整细节，请参考法规。 AMPLIFY™ TY 1353 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1353 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates. Main Characteristics: Excellent adhesion to polyamide and EVOH Excellent physical properties Wide range of process and service temperature For blown and cast film Complies with: US FDA 21 CFR 175.105 EU, No 10/2011 Consult the regulations for complete details. |
产品描述 Product Description
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.921 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ASTM D1238 |
|
MAH 接枝水平 MAH grafting level 2 |
Low | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D638 | ||
|
屈服 yield |
11.0 | MPa | ASTM D638 |
|
断裂 fracture |
27.6 | MPa | ASTM D638 |
|
弯曲模量 Flexural Modulus |
|||
|
2% 正割 2% secant |
MPa | ASTM D790 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
膜耐刺穿性 Membrane puncture resistance |
|||
|
51 µm 51 µm |
J/cm³ | 内部方法 | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
2% 正割，MD：51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
|
2% 正割，TD：51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服，51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
|
TD，屈服，51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
|
MD，断裂，51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
|
TD，断裂，51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
断裂 fracture |
% | ASTM D638 | |
|
MD，断裂，51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
|
TD，断裂，51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
|
落锤冲击 Gardner Impact |
|||
|
51 µm 51 µm |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ASTM D1922 | ||
|
MD：51 µm MD：51 µm |
g | ASTM D1922 | |
|
TD：51 µm TD：51 µm |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，50.8 µm 45°，50.8 µm |
ASTM D2457 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| 3 Method B |
|
【新闻资讯】查看全部 
Science用微波炉烤1秒钟造出高质量石墨烯
2016-09-07 据报道，美国罗格斯大学的研究团队开发出一种新型微波方法法制备高质量的石墨烯材料，很牛逼地说，科研人员将氧化石墨烯（graphene oxide）放入1000瓦功率的微波炉中，烤上1秒钟后，就得到几乎不含氧的极高质量的石墨烯（graphene）成品。(氧化石墨烯到石墨烯啊!!!)牛逼的工作不需要更多的文字去描述它，大家有兴趣就看文献去吧!!! |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付