牌号简介 About |
---|
Radel® R-5000是一种透明的聚苯砜(PPSU),具有优异的水解稳定性和韧性,优于其他商用高温工程树脂。该树脂还提供高偏转温度和优异的抗环境应力开裂性能。Radel聚合物具有固有的阻燃性,具有优异的热稳定性和良好的电气性能。烟雾:Radel® R-5000 cl 301琥珀色:Radel® R-5000 nt蓝色:Radel® R-5000 tr bu391 Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins. This resin also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties. Smoke: Radel® R-5000 CL 301 Amber: Radel® R-5000 NT Blue: Radel® R-5000 TR BU391 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.29 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
365℃,5.0kg 365℃,5.0kg |
14 to 20 | g/10min | ASTM D1238 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
0.70 | % | ASTM D955 |
吸水率 Water Absorption |
|||
平衡 Equilibrium Balancing Equilibrium |
1.1 | % | ASTM D570 |
24hr 24hr |
0.37 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸强度 Tensile Strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 brk,3.18 mm Broken BRK, 3.18 mm |
% | ASTM D638 | |
屈服 yld,3.18 mm Yield yld, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Flexural Modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
|||
5% 应变,3.18 mm 5% strain, 3.18 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
拉伸冲击强度 Tensile Impact Strength |
|||
3.18 mm 3.18 mm |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
玻璃化转变温度 Glass Transition Temperature |
℃ | ASTM E1356 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
相对温度指数 Relative Temp Index(RTI) |
|||
电气, 0.36 mm elec, 0.36 mm |
℃ | UL746B | |
电气, 0.75 mm elec, 0.75 mm |
℃ | UL746B | |
电气, 1.5 mm elec, 1.5 mm |
℃ | UL746B | |
电气, 3 mm elec, 3 mm |
℃ | UL746B | |
冲击, 0.36 mm imp, 0.36 mm |
℃ | UL746B | |
冲击, 0.75 mm imp, 0.75 mm |
℃ | UL746B | |
冲击, 1.5 mm imp, 1.5 mm |
℃ | UL746B | |
冲击, 3 mm imp, 3 mm |
℃ | UL746B | |
强度, 0.36 mm str, 0.36 mm |
℃ | UL746B | |
强度, 0.75 mm str, 0.75 mm |
℃ | UL746B | |
强度, 1.5 mm str, 1.5 mm |
℃ | UL746B | |
强度, 3 mm str, 3 mm |
℃ | UL746B | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength |
ASTM D149 | ||
0.0254 mm 0.0254 mm |
kV/mm | ASTM D149 | |
3.18 mm 3.18 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant |
|||
3.18 mm,60 Hz 3.18 mm,60 Hz |
ASTM D150 | ||
热丝引燃 Hot Wire Ignition |
|||
0.36 mm 0.36 mm |
UL 746A | ||
0.75 mm 0.75 mm |
UL 746A | ||
1.5 mm 1.5 mm |
UL 746A | ||
3.0 mm 3.0 mm |
UL 746A | ||
高电弧燃烧指数 HAI |
|||
0.36 mm 0.36 mm |
UL 746A | ||
0.75 mm 0.75 mm |
UL 746A | ||
1.5 mm 1.5 mm |
UL 746A | ||
3.0 mm 3.0 mm |
UL 746A | ||
相比漏电起痕指数 Comparative Tracking Index |
UL 746A | ||
高电压电弧起痕速率 High Voltage Arc Track Rate |
UL 746A | ||
耐电弧性 Arc Resistance |
ASTM D495 | ||
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive Index |
ASTM D542 | ||
补充信息 Supplementary Information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Steam Sterilization(w/ Morpholine) Steam Sterilization(w/ Morpholine) |
Cycles | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
0.36 mm 0.36 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.5 mm 1.5 mm |
UL 94 | ||
3 mm 3 mm |
UL 94 |
备注 |
---|
1 NSF STD-51 compliant for NT only. |
2 Tested at 82 °C (180 °F) (Commercial Hot) |
3 一般属性:这些不能被视为规格。 |
4 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
5 周期完成,无开裂、裂纹或破裂。 蒸气消毒条件: - 温度:270 °F(132 °C) - 时间: 30分钟/周期 - 蒸汽压力: 27 PSIG (0.19兆帕) -应力水平:弯曲1000 psi (7.0兆帕) - 添加剂:50 ppm吗啉 |
【新闻资讯】查看全部 ![]()
热搜第一!星巴克宣布将退出俄罗斯市场,关闭130家门店,并不再保留
2022-05-24 5月24日早间,星巴克宣布将退出俄罗斯市场话题登上微博热搜榜第一。 央视财经官方微博5月24日消息,据美国ABC新闻网5月23日报道,美国星巴克公司宣布将退出俄罗斯市场。星巴克当天 |
热搜第一!星巴克宣布将退出俄罗斯市场,关闭130家门店,并不再保留 5月24日早间,“星巴克宣布将退出俄罗斯市场”话题登上微博热搜榜第一。 央视财经官方微博5月24日消息,据美国ABC新闻网5月23日报道,美国星巴克公司宣布将退出俄罗斯市场。星巴克当天在给员工们的备忘录中表示,决定关闭其在俄罗斯的130家门店,其品牌在俄罗斯市场上也将不再保留。 不过,星巴克表示,将向其近2000名俄罗斯员工支付6个月的工资,并帮助他们过渡到新工作岗位。星巴克自3月8日起,暂停了在俄罗斯的所有门店业务。 此前在3月8日,麦当劳宣布将暂时关闭俄罗斯境内的850家门店,但是会继续支付员工工资。当日,星巴克公司、可口可乐公司也宣布暂停在俄罗斯的业务。 据报道,麦当劳在声明中称,该公司“正在寻求将其在俄罗斯的全部麦当劳餐厅一同出售给当地买家”,并补充说,尽管该公司将继续在俄罗斯保留商标,但现有门店将不再使用麦当劳的名称、标识、品牌和菜单。 据法新社报道,当地时间5月16日,美国餐饮连锁公司麦当劳宣布,该公司最终决定退出俄罗斯市场。 据财联社,俄罗斯联邦安全会议副主席梅德韦杰夫3月10日在谈及外国公司大规模撤离俄罗斯市场时表示,政府正在研究回应措施,其中包括将撤离的外国公司的资产进行破产和国有化等措施。 自一些国际品牌宣布退出俄罗斯市场后,都将陆续被俄罗斯本土企业接管。从另一个层面上来讲,这的确是俄罗斯企业千载难逢的好机会。 上周四(5月19日),麦当劳同意将俄罗斯业务出售给目前的特许经营权持有人、西伯利亚商人Alexander Govor。根据协议,Govor将收购麦当劳的所有分店,并以新品牌经营。市场预计“俄罗斯版”麦当劳将很快面世。 而“俄版”的可口可乐已经抢跑。上周一(5月16日),俄罗斯饮料生产商Ochakovo推出了一系列新的软饮料,以替代离开俄罗斯市场的标志性品牌可口可乐。 不仅是美国企业,法国汽车制造商雷诺也于上周一表示,同意将把雷诺俄罗斯公司(Renault Russia)的全部股权出售给莫斯科市政府,并将所持AvtoVAZ的67.69%股权出售给俄罗斯政府支持的汽车研发中心NAMI。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
加工方式 | |||
---|---|---|---|
注塑成型 Injection Molding | Nominal Value | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
熔体温度 Melt Temperature | °C | ||
模具温度 Mold Temperature | °C | ||
螺杆压缩比 Screw Compression Ratio | |||
挤出成型 Extrusion Molded | Nominal Value | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
料筒-1区温度 Barrel - Zone 1 Temperature | °C | ||
料筒-2区温度 Barrel - Zone 2 Temperature | °C | ||
料筒-3区温度 Barrel - Zone 3 Temperature | °C | ||
料筒-4区温度 Barrel - Zone 4 Temperature | °C | ||
料筒-5区温度 Barrel - Zone 5 Temperature | °C | ||
适配器温度 Adapter Temperature | °C | ||
熔体温度 Melt Temperature | °C | ||
模具温度 Die Temperature | °C |