牌号简介 About |
---|
Grivory® HT2V-3X V0 nat 6059是一种Polyamide 6T/66 Copolymer (Nylon 6T/66)材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Grivory® HT2V-3X V0 nat 6059的主要特性有: 阻燃/额定火焰 Flame Retardant 耐化学品 耐热 优良的脱模剂 典型应用领域包括: 电气/电子应用 汽车行业 电气用具 工程/工业配件 工具 Grivory® HT2V-3X V0 nat 6059 is a Polyamide 6T/66 Copolymer (Nylon 6T/66) material filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grivory® HT2V-3X V0 nat 6059 are: Flame Rated Flame Retardant Chemical Resistant Good Mold Release Heat Resistant Typical applications include: Automotive Electrical/Electronic Applications Appliances Engineering/Industrial Parts Lighting Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ISO 1183 |
收缩率 Shrinkage |
|||
MD MD |
0.10 | % | ISO 294-4 |
TD TD |
0.90 | % | ISO 294-4 |
吸水率 Water Absorption |
|||
23℃,24hr 23℃,24hr |
3.5 | % | ISO 62 |
23℃,50% RH 23℃,50% RH |
1.3 | % | ISO 62 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
维卡软化温度 Vicat Softening Temperature |
|||
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
TD TD |
1/℃ | ISO 11359-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volume Resistivity |
Ω.cm | IEC 60093 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | IEC 60243-1 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) |
|||
1 mm 1 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
2 mm 2 mm |
℃ | IEC 60695-2-12 | |
3 mm 3 mm |
℃ | IEC 60695-2-12 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
1.00mm 1.00mm |
℃ | IEC 60695-2-13 | |
1.50mm 1.50mm |
℃ | IEC 60695-2-13 | |
2.00mm 2.00mm |
℃ | IEC 60695-2-13 | |
3.00mm 3.00mm |
℃ | IEC 60695-2-13 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 ball-indentation hardness |
MPa | ISO 2039-1 | |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Long Term |
3 Short Term |
4 10°C/min |
【新闻资讯】查看全部
8月份化工原料价钱同比下降2.5%
2016-09-13 国家统计局9月9日发布的2016年8月份工业生产者出厂价格指数(PPI)数据显示,PPI环比上涨0.2%,同比下降0.8%。工业生产者购进价格环比上涨0.2%,同比下降1.7%。 工业生产者出厂价格中,生产资料价格同比下降1.0%,影响全国工业生产者出厂价格总水平下降约0.8个百分点。其中,采掘工业价格下降3.2%,原材料工业价格下降2.3%,加工工业价格下降0.4%。生活资料价格同比持平(涨跌幅度为0,下同)。其中,食品价格上涨0.1%,衣着价格上涨0.8%,一般日用品价 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |