| Viton® AL-600是一种“Al族”胶聚合物,与前体Viton B-70N相比,其加工性能得到了改善。这种胶提供:更高的粘度改善了模具流动性,更好的模具释放,更少的模具污染改善了压缩永久性,以及良好的低温特性应用燃油系统,如喷油器O形环。当使用胶聚合物混合物作为织物和其他基材的溶液涂层时,O型环、垫圈和其他密封装置的注射和转移成型-挤压绳索、型材和管道或压延板。 Viton® AL-600 is an "AL-family" gum polymer that demonstrates improved processing when compared to its precursor Viton® B-70N. This gum provides: Higher viscosity Improved mold flow Better mold release Less mold fouling Improved compression set resistance, and Good low temperature characteristics Applications Fuel systems, such as fuel injectors O-rings Injection and transfer molding of O-rings, gaskets, and other sealing devices Extruded cords, profiles and tubing, or calendered sheets, when a blend of gum polymers are used Solution coatings of fabrics and other substrates. |
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.77 | g/cm³ | ASTM D792 |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+10,121℃ ML 1+10,121℃ |
60 | MU | ASTM D1646 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A,23℃ Shore A, 23 ℃ 2 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,23℃ Shore A, 23 ℃ 3 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,23℃ Shore A, 23 ℃ 4 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,23℃ Shore A, 23 ℃ 5 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,23℃ Shore A, 23 ℃ 6 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,23℃ Shore A, 23 ℃ 7 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,23℃ Shore A, 23 ℃ 8 |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
ASTM D412 | |
|
100% 应变,23℃ 100% strain, 23 ℃ 9 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,23℃ 100% strain, 23 ℃ 10 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,23℃ 100% strain, 23 ℃ 11 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,23℃ 100% strain, 23 ℃ 12 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,23℃ 100% strain, 23 ℃ 13 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,23℃ 100% strain, 23 ℃ 14 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,23℃ 100% strain, 23 ℃ 15 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
ASTM D412 | |
|
屈服,23℃ Yield, 23 ℃ 9 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
屈服,23℃ Yield, 23 ℃ 10 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
屈服,23℃ Yield, 23 ℃ 11 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
屈服,23℃ Yield, 23 ℃ 12 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
屈服,23℃ Yield, 23 ℃ 13 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
屈服,23℃ Yield, 23 ℃ 14 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
屈服,23℃ Yield, 23 ℃ 15 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
ASTM D412 | |
|
断裂,23℃ Fracture, 23 ℃ 9 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
断裂,23℃ Fracture, 23 ℃ 10 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
断裂,23℃ Fracture, 23 ℃ 11 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
断裂,23℃ Fracture, 23 ℃ 12 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
断裂,23℃ Fracture, 23 ℃ 13 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
断裂,23℃ Fracture, 23 ℃ 14 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
断裂,23℃ Fracture, 23 ℃ 15 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
撕裂强度 tear strength 16 |
注册或登录后
所有资料免费
|
||
|
23℃ 23℃ 16 |
注册或登录后
所有资料免费
|
kN/m | ASTM D624 |
|
压缩形变 Compression deformation |
注册或登录后
所有资料免费
|
ASTM D395B | |
|
150℃,70 hr 150℃,70 hr |
注册或登录后
所有资料免费
|
% | ASTM D395B |
|
200℃,70 hr 200℃,70 hr |
注册或登录后
所有资料免费
|
% | ASTM D395B |
|
200℃,168 hr 200℃,168 hr |
注册或登录后
所有资料免费
|
% | ASTM D395B |
|
232℃,22 hr 232℃,22 hr |
注册或登录后
所有资料免费
|
% | ASTM D395B |
|
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积变化 Volume change |
注册或登录后
所有资料免费
|
ASTM D471 | |
|
23℃,168 hr,in M15(Fuel C/Methanol 85/15) 23℃,168 hr,in M15(Fuel C/Methanol 85/15) |
注册或登录后
所有资料免费
|
% | ASTM D471 |
|
200℃,70 hr,在IRM 903油中 200 ℃, 70 hr, in IRM 903 oil |
注册或登录后
所有资料免费
|
% | ASTM D471 |
| 备注 |
|---|
| 1 一般属性:这些不能被视为规格。 |
| 2 20 in/min, 老化 M15 (Fuel C/Methanol 85/15) 168 hr 在 73°F |
| 3 20 in/min, 老化 70 hr 在 392°F |
| 4 20 in/min, 老化 IRM 903 Oil 70 hr 在 392°F |
| 5 20 in/min, 老化 168 hr 在 392°F |
| 6 20 in/min, 老化 24 hr 在 450°F |
| 7 20 in/min, 老化 70 hr 在 482°F |
| 8 20 in/min, 老化 168 hr 在 482°F |
| 9 C 模具 |
| 10 老化 M15 (Fuel C/Methanol 85/15) 168 hr 在 73°F |
| 11 老化 70 hr 在 392°F |
| 12 老化 IRM 903 Oil 70 hr 在 392°F |
| 13 老化 168 hr 在 392°F |
| 14 老化 24 hr 在 450°F |
| 15 老化 70 hr 在 482°F |
| 16 老化 168 hr 在 482°F |
|