| 牌号简介 About |
|---|
| Lotader 4503是一种乙烯、丙烯酸酯和马来酸酐的无规三元共聚物，经高压釜聚合而成。应用洛塔德4503是一种多用途的挤出层压粘合剂，设计为一个现成的树脂使用纯。Lotader 4503对普通、无底漆的Opet膜以及其他塑料膜（如Opp、CPP、Opa和反向印刷膜）具有极好的粘合性。它还可以粘合到更容易的基材上，如聚乙烯薄膜、铝箔、金属化塑料、纸和纸板。典型用途是：极性和非极性薄膜和箔的挤压层压粘合剂，特别是用于欧佩特和铝。用于LDPE/TIE/EVOH或PA/TIE共挤涂层的粘合剂，可涂在OPET或其他薄膜上。 LOTADER® 4503 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications LOTADER® 4503 is a versatile adhesive for extrusion lamination, designed as a ready for use resin to be used pure. LOTADER® 4503 gives excellent adhesion to plain, primer-less OPET films as well as to other plastic films like OPP, CPP, OPA and reverse-printed films. It also bonds to easier substrates like PE films, aluminium foil, metalized plastics, paper and board. Typical uses are: Adhesive for extrusion lamination of polar and non-polar films and foils, particularly for OPET and aluminium. Adhesive for coextrusion coating of LDPE / Tie / EVOH or PA / tie onto OPET or other films. |
产品描述 Product Description
用途：层压板;粘合剂;涂层应用;
加工条件：共挤出成型
性能特点： 热稳定性好; 熔体稳定性高; 粘结性好; 内缩量低; 易剥离; 三元共聚物; Good dissection,Low shrinkage,Good bond,Terpolymer,Heat Stabilized,Higher melt stability
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
|
密度 Density |
0.940 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
8.0 | g/10min | ISO 1133 |
|
190℃，2.16kg 190℃，2.16kg |
8.0 | g/10min | ASTM D1238 |
|
甲基丙烯酸含量 Methacrylic acid content |
20.0 | wt% | |
|
马来酸酐含量 Maleic anhydride content |
wt% | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
ISO 868 | ||
|
邵氏 D，模压成型 Shaw's D, molded |
ASTM D2240 | ||
|
拉伸强度 tensile strength |
|||
|
断裂，模压成型 Fracture, molded |
MPa | ASTM D638 | |
|
断裂，模压成型 Fracture, molded |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，模压成型 Fracture, molded |
% | ASTM D638 | |
|
断裂，模压成型 Fracture, molded |
% | ISO 527-2 | |
|
弯曲模量 Flexural Modulus |
|||
|
模压成型 Compression Molding |
MPa | ISO 178 | |
|
模压成型 Compression Molding |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 2 | |
|
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部
雀巢热巧可可粉改用纸质包装
2019-01-23 年营收近千亿美元的Nestlé(瑞士雀巢公司)是世界第一大食品饮料企业，去年收购星巴克后，雀巢的商业版图更加霸道。 不过，第一总是要起到带头模范作用，何况是攸关企业责任感的环保议题。 此前，雀巢制定了可持续发展目标，即在2025年前实现100%使用可再生材料包装物。如今，第一步即将迈开。 从今年2月份开始，雀巢将开始淘汰塑料吸管，取而代的是纸质吸管或其它创新设计。同时，大约今年Q1某个时间，雀巢经典产品Nesquik热巧可可粉会改用纸质包装。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付